Formation, thermal stability, mechanical properties and corrosion resistance of Cu-Zr-Ti-Ni-Nb bulk glassy alloys

Tsuyoshi Yamamoto, Chunling Qin, Tao Zhang, Katsuhiko Asami, Akihisa Inoue

研究成果: Contribution to journalArticle査読

26 被引用数 (Scopus)

抄録

Bulk glassy alloys exhibiting high strength and good corrosion resistance were formed in (Cu0.6Zr0.3Ti0.1)100-x-y NiyNbx systems. The bulk glassy alloy rods with a diameter of 3 mm are formed in a wide composition range of 0 to 6 at%Ni and 0 to 6 at%Nb by copper mold casting. As the Nb content increases, the glass transition temperature (Tg) increases while the crystallization temperature (Tx) decreases, resulting in a decrease in ΔTx (= Tx - Tg) from 60 K at 0 at%Nb to 36 K at 5 at%Nb. The high fracture strength (σc,f) exceeding 2000 MPa is obtained for the Cu-Zr-Ti-Ni-Nb alloys containing more than 3 at%Nb and their high strength alloys also exhibit distinct plastic elongation of 0.2 to 0.8%. The corrosion resistance of the Cu-Zr-Ti bulk glassy alloy is also significantly improved by the simultaneous addition of Ni and Nb and no loss in sample weight in 1 N HCl and 3%NaCl solutions is detected for the Cu-Zr-Ti-Ni-Nb alloys containing 5 at%Ni and 6 at%Nb or 2 at%Nb, respectively. The usefulness of the simultaneous addition of Ni and Nb on the σc,f and corrosion loss in conjunction with high glass-forming ability seems to affect significant influence on the future development of bulk glassy alloys with special functional characteristics.

本文言語英語
ページ(範囲)1147-1152
ページ数6
ジャーナルMaterials Transactions
44
6
DOI
出版ステータス出版済み - 6 2003
外部発表はい

All Science Journal Classification (ASJC) codes

  • 材料科学(全般)
  • 凝縮系物理学
  • 材料力学
  • 機械工学

フィンガープリント

「Formation, thermal stability, mechanical properties and corrosion resistance of Cu-Zr-Ti-Ni-Nb bulk glassy alloys」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル