Four-dimensional observation of ductile fracture in sintered iron using synchrotron x-ray laminography

Y. Ozaki, Y. Mugita, M. Aramaki, O. Furukimi, S. Ooue, F. Jiang, T. Tsuji, A. Takeuchi, M. Uesugi, K. Ashizuka

研究成果: 著書/レポートタイプへの貢献会議での発言

抜粋

Synchrotron X-ray laminography was used to reveal the time evolution of the three-dimensional (3D) morphology of micropores in sintered iron during a tensile test. 3D snapshots showed networked open pores growing wider than 20 µm along the tensile direction, resulting in internal necking of the specimen. Finally, these pores initiated cracks perpendicular to the tensile direction by coalescing with surrounding preexisting microvoids or secondary-generated voids immediately before fracture. Topological analysis of the barycentric positions of these microvoids showed that they formed two-dimensional networks within a ~20 µm-radius area. This indicates that microvoid coalescence could occur on shear planes formed close to the enlarged open pores or between closed pores by strain accumulation and play an important role in crack initiation.

元の言語英語
ホスト出版物のタイトルEuro PM 2018 Congress and Exhibition
出版者European Powder Metallurgy Association (EPMA)
ISBN(電子版)9781899072507
出版物ステータス出版済み - 1 1 2020
イベントEuropean Powder Metallurgy Congress and Exhibition, Euro PM 2018 - Bilbao, スペイン
継続期間: 10 14 201810 18 2018

出版物シリーズ

名前Euro PM 2018 Congress and Exhibition

会議

会議European Powder Metallurgy Congress and Exhibition, Euro PM 2018
スペイン
Bilbao
期間10/14/1810/18/18

    フィンガープリント

All Science Journal Classification (ASJC) codes

  • Metals and Alloys
  • Surfaces, Coatings and Films
  • Surfaces and Interfaces

これを引用

Ozaki, Y., Mugita, Y., Aramaki, M., Furukimi, O., Ooue, S., Jiang, F., ... Ashizuka, K. (2020). Four-dimensional observation of ductile fracture in sintered iron using synchrotron x-ray laminography. : Euro PM 2018 Congress and Exhibition (Euro PM 2018 Congress and Exhibition). European Powder Metallurgy Association (EPMA).