Fracture mechanism in fatigue of Ni-base superalloy Inconel 718 at elevated temperatures

Norio Kawagoishi, Nu Yan, Masahiro Goto, Qiang Chen, Qingyuan Wang, Yoshihisa Ohzono

研究成果: Contribution to journalArticle査読

3 被引用数 (Scopus)

抄録

In order to investigate the fracture mechanism in fatigue of Ni-base Superalloy at elevated temperatures, rotating bending fatigue tests were carried out for Inconel 718 at 500°C and 600°C up to 108 cycles. At both temperatures, fracture occurred from a subsurface of the specimen in long life region, though the origin of fracture was the specimen surface in short life region. Consequently, S-N curves showed a two-step shape in elevated temperature tests. Although a surface crack was observed similar to the result at room temperature even in long life region at elevated temperatures, the surface crack stopped propagating. In this case, interganular cracks were observed at an origin of subsurface fracture. The subsurface damage was initiated at the early stage of fatigue life.

本文言語英語
ページ(範囲)1226-1233
ページ数8
ジャーナルNihon Kikai Gakkai Ronbunshu, A Hen/Transactions of the Japan Society of Mechanical Engineers, Part A
71
9
DOI
出版ステータス出版済み - 9 2005
外部発表はい

All Science Journal Classification (ASJC) codes

  • 材料科学(全般)
  • 材料力学
  • 機械工学

フィンガープリント

「Fracture mechanism in fatigue of Ni-base superalloy Inconel 718 at elevated temperatures」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル