Fretting fatigue under variable amplitude loading below fretting fatigue limit

Yoshiyuki Kondo, Chu Sakae, Masanobu Kubota, Hiroki Kitahara, Kazutoshi Yanagihara

研究成果: Contribution to journalArticle

3 引用 (Scopus)

抜粋

The fatigue limit diagram shows the allowable stress zone for constant amplitude fatigue loading. It was shown is this study that fretting fatigue failure occured in the case of variable amplitude loading condition even when every stress amplitude was kept below the fretting fatigue limit diagram. The reason why such a phenomenon occurred was examined using repeated two-step loading fretting fatigue test. The first step stress of the repeated two-step loading was chosen as R= -1 and the second step stress was with high mean stress. A non-propagating crack was formed by the first step stress even well below the fatigue limit. This crack functioned as a pre-crack for the second step stress with high mean stress. Consequently, fatigue failure did occur even when every stress was kept below the fretting fatigue limit diagram of constant amplitude. The fatigue limit diagram does not necessarily guarantee the safety in the case of variable amplitude loading.

元の言語英語
ページ(範囲)763-768
ページ数6
ジャーナルNihon Kikai Gakkai Ronbunshu, A Hen/Transactions of the Japan Society of Mechanical Engineers, Part A
71
発行部数5
出版物ステータス出版済み - 5 2005

All Science Journal Classification (ASJC) codes

  • Mechanical Engineering

フィンガープリント Fretting fatigue under variable amplitude loading below fretting fatigue limit' の研究トピックを掘り下げます。これらはともに一意のフィンガープリントを構成します。

  • これを引用