Friction behavior of high-density poly(2-methacryloyloxyethyl phosphorylcholine) brush in aqueous media

Motoyasu Kobayashi, Yuki Terayama, Nao Hosaka, Masataka Kaido, Atsushi Suzuki, Norifumi Yamada, Naoya Torikai, Kazuhiko Ishihara, Atsushi Takahara

研究成果: ジャーナルへの寄稿学術誌査読

219 被引用数 (Scopus)

抄録

Super-hydrophilic polymer brushes were prepared by surface-initiated atom transfer radical polymerization of 2-methacryloyloxyethyl phosphorylcholine (MPC) on initiator-immobilized silicon wafers. The graft density was estimated to be ca. 0.22 chains nm-2 based on the linear relationship between Mn and the layer thickness. The contact angle against water was very low, and air bubbles in water hardly attached onto the brush surface, indicating a super-hydrophilic surface. Neutron reflectivity measurements of the poly(MPC) brush showed that the grafting polymer chains extended a fair amount in the vertical direction from the substrate in a good solvent such as water, while they shrunk in a poor solvent. Frictional properties of the poly(MPC) brushes were characterized by sliding a glass ball probe in air and various solvents under a load of 0.49 N at a sliding velocity of 90 mm min-1. An extremely low friction coefficient of the poly(MPC) brush was observed in humid atmosphere because water molecules adsorbed into the brush layer acted as a lubricant.

本文言語英語
ページ(範囲)740-746
ページ数7
ジャーナルSoft Matter
3
6
DOI
出版ステータス出版済み - 5月 28 2007

!!!All Science Journal Classification (ASJC) codes

  • 化学 (全般)
  • 凝縮系物理学

フィンガープリント

「Friction behavior of high-density poly(2-methacryloyloxyethyl phosphorylcholine) brush in aqueous media」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル