Gaseous hydrogen embrittlement of a Ni-free austenitic stainless steel containing 1 mass% nitrogen: Effects of nitrogen-enhanced dislocation planarity

Motomichi Koyama, Kishan Habib, Takuro Masumura, Toshihiro Tsuchiyama, Hiroshi Noguchi

研究成果: ジャーナルへの寄稿記事

抜粋

We investigated the effect of hydrogen on degradation of tensile properties in a Fe–25Cr–1N austenitic stainless steel. Hydrogen was introduced by exposure to a hydrogen gas atmosphere at 100 MPa and 270 °C. Hydrogen charging caused significant ductility loss associated with nitrogen-enhanced dislocation planarity. Specifically, even without hydrogen, the nitrogen-enhanced planar dislocation glide induced micro-stress concentration, which assisted the occurrence of hydrogen-induced intergranular and quasi-cleavage fractures. The hydrogen-assisted intergranular cracking occurred along boundaries of grains where primary slip was predominantly activated. On the other hand, the hydrogen-assisted quasi-cleavage fracture took place when multiple slip systems were activated. The hydrogen-related cracks emerged, but their growth was arrested via crack blunting associated with a significant plastic deformation. Instead, new cracks formed near the crack tips. Therefore, hydrogen-assisted crack propagation occurred through repetition of crack blunting, initiation, and coalescence.

元の言語英語
ページ(範囲)10209-10218
ページ数10
ジャーナルInternational Journal of Hydrogen Energy
45
発行部数16
DOI
出版物ステータス出版済み - 3 20 2020

    フィンガープリント

All Science Journal Classification (ASJC) codes

  • Renewable Energy, Sustainability and the Environment
  • Fuel Technology
  • Condensed Matter Physics
  • Energy Engineering and Power Technology

これを引用