Generation and transportation mechanisms for two-dimensional hole gases in GaN/AlGaN/GaN double heterostructures

Akira Nakajima, Pucheng Liu, Masahiko Ogura, Toshiharu Makino, Kuniyuki Kakushima, Shinichi Nishizawa, Hiromichi Ohashi, Satoshi Yamasaki, Hiroshi Iwai

研究成果: Contribution to journalArticle査読

21 被引用数 (Scopus)

抄録

The electrical properties of two-dimensional hole gases (2DHGs) in GaN/AlGaN/GaN double heterostructures were investigated. The layers were grown on sapphire substrates and a high-quality bulk GaN substrate. The coexistence of 2DHG and 2D electron gases on both sides of the AlGaN layer was confirmed by Hall effect measurements at 80-460 K. It was also verified that the 2DHGs were generated by negative polarization at the undoped GaN/AlGaN interface, which did not have a doped Mg acceptor. It was also demonstrated that the 2DHG density could be controlled by varying the AlGaN layer thickness and was inversely related to the 2DHG mobility. The measured relation indicated that the 2DHG mobility is mainly limited by phonon scatterings at around room temperature. As a result, the maximum 2DHG mobility of 16 cm/Vs at 300 K was achieved with a density of 1 × 10 cm-2.

本文言語英語
論文番号153707
ジャーナルJournal of Applied Physics
115
15
DOI
出版ステータス出版済み - 4 21 2014
外部発表はい

All Science Journal Classification (ASJC) codes

  • Physics and Astronomy(all)

フィンガープリント 「Generation and transportation mechanisms for two-dimensional hole gases in GaN/AlGaN/GaN double heterostructures」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル