Geometrically induced giant magnetoresistance behavior in quarter-micrometer strip pattern

K. Matsuyama, K. Matsuo, Y. Nozaki

研究成果: Contribution to journalConference article査読

3 被引用数 (Scopus)

抄録

The present article reports a geometrically induced magnetoresistance (MR) behavior observed in magnetic strips consisting of a symmetric layer structure with lateral sizes down to 0.2 μm. The MR ratio was markedly improved from 2.8% for an as-grown film of Co(6 nm)/Cu(6 nm)/Co(6 nm) to 4.6% by structuring it into a strip with 0.3 μm width. The parabolic MR behavior observed in the hard-axis direction suggests that the magnetization in the two magnetic layers rotates toward the opposite directions, which can be explained by the magnetostatic interaction between the surface magnetic charges at the pattern edges. The dependence of MR saturation field on the pattern width agrees well with a theoretical prediction based on a coherent rotation model. The MR ratio was markedly increased by the increase of the layer number and the thickness of the magnetic layer, the highest value of 7.8% was obtained for a strip made of [Co(6nm)/Cu(4nm)]2Co(6nm). A linear-and hysteresis-free MR response was performed with an alternative field modulation under a transverse bias field.

本文言語英語
ページ(範囲)5474-5476
ページ数3
ジャーナルJournal of Applied Physics
85
8 II B
DOI
出版ステータス出版済み - 4 15 1999
イベントProceedings of the 43rd Annual Conference on Magnetism and Magnetic Materials - Miami, FL, 米国
継続期間: 11 9 199811 12 1998

All Science Journal Classification (ASJC) codes

  • Physics and Astronomy(all)

フィンガープリント 「Geometrically induced giant magnetoresistance behavior in quarter-micrometer strip pattern」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル