Growth of high-quality ErBa2Cu3O7-δ thin films

T. Ohazama, M. Mukaida, A. Ichinose, K. Matsumoto, Y. Yoshida, S. Horii, A. Saito, S. Ohshima

研究成果: ジャーナルへの寄稿学術誌査読

14 被引用数 (Scopus)

抄録

ErBa2Cu3O7-δ thin films are grown by pulsed laser deposition (PLD). Using a SrTiO3 as a lattice matched substrate. In the film growth, the substrate temperature is varied from 720 to 780 °C. From X-ray diffraction (XRD) patterns, only the 00l reflections from the ErBa2Cu3O7-δ films are observed. The average of the c-axis length of the other films is 11.6875 Å. ErBa 2Cu3O7-δ film grown at 735 °C is excellent in the crystallinity, while the intensity of 00l peaks of the film grown at more than 780 °C obviously weakened. The zero resistance T c is 90.5 K. Superconducting transition width is 1.5 K. Large and flat grains are observed by atomic force microscopy (AFM) at the surface of the film. From the scanning electron microscope (SEM) image, we confirmed some grains with the size of approximately 200 nm in diameter on the ErBa 2Cu3O7-δ thin film. We observe the interface of ErBa2Cu3O7-δ and substrate clearly by transmission electron microscopy (TEM) measurements.

本文言語英語
ページ(範囲)1301-1305
ページ数5
ジャーナルPhysica C: Superconductivity and its applications
412-414
SPEC. ISS.
DOI
出版ステータス出版済み - 10月 2004
外部発表はい

!!!All Science Journal Classification (ASJC) codes

  • 電子材料、光学材料、および磁性材料
  • 凝縮系物理学
  • エネルギー工学および電力技術
  • 電子工学および電気工学

フィンガープリント

「Growth of high-quality ErBa2Cu3O7-δ thin films」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル