High critical current YBCO thick films by TFA-MOD process

Yoshitaka Tokunaga, Hiroshi Fuji, Ryo Teranishi, Junko Shibata, Sigenobu Asada, Tetsuji Honjo, Teruo Izumi, Yuh Shiohara, Yasuhiro Iijima, Takashi Saitoh

研究成果: Contribution to journalConference article査読

25 被引用数 (Scopus)

抄録

As a method of the fabrication processes of YBa2Cu 3O7-x (YBCO), the metalorganic deposition (MOD) process using metal trifluoroacetete (TFA) is considered to be a strong candidate due to its low cost fabrication process for coated conductors with high J c. In our previous work, a triple coated film with 1 μm in thickness was fabricated on a CeO2/IBAD-YSZ layer buffered Hastelloy substrate by optimizing the condition of heat treatments such as P H2O in the multi-coating method [Physica C 378-381 (2002) 1013]. The Jc value of 1.6 MA/cm2 (77 K in self-field) in this film patterned 100 μm width and the I*c value of 153 A/cm-width at 77 K in self-field were achieved. In order to obtain a thicker film with high overall I*c for 1 cm width, the influence of the heat treatment conditions of PH2O, PO2, and the temperature in the MOD process was investigated. Subsequently, a 5 times coated film was obtained on a CeO2/IBAD-Zr2Gd2O7 layer buffered Hastelloy substrate by optimizing the conditions of heating and dip coating. As a result, the overall transport Ic value was improved to 210 A and Jc value of 1.53 MA/cm2 was obtained (77 K in self-field).

本文言語英語
ページ(範囲)909-912
ページ数4
ジャーナルPhysica C: Superconductivity and its applications
392-396
PART 2
DOI
出版ステータス出版済み - 10 2003
外部発表はい
イベントProceedings of the 15th International Symposium on Superconduc - Yokohama, 日本
継続期間: 11 11 200211 13 2002

All Science Journal Classification (ASJC) codes

  • Electronic, Optical and Magnetic Materials
  • Condensed Matter Physics
  • Energy Engineering and Power Technology
  • Electrical and Electronic Engineering

フィンガープリント 「High critical current YBCO thick films by TFA-MOD process」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル