High heat flux properties of pure tungsten and plasma sprayed tungsten coatings

X. Liu, S. Tamura, K. Tokunaga, N. Yoshida, N. Noda, L. Yang, Z. Xu

研究成果: Contribution to journalConference article査読

37 被引用数 (Scopus)

抄録

High heat flux properties of pure tungsten and plasma sprayed tungsten coatings on carbon substrates have been studied by annealing and cyclic heat loading. The recrystallization temperature and an activation energy Q R = 126 kJ/mol for grain growth of tungsten coating by vacuum plasma spray (VPS) were estimated, and the microstructural changes of multi-layer tungsten and rhenium interface pre-deposited by physical vapor deposition (PVD) with anneal temperature were investigated. Cyclic load tests indicated that pure tungsten and VPS-tungsten coating could withstand 1000 cycles at 33-35 MW/m2 heat flux and 3 s pulse duration, and inert gas plasma spray (IPS)-tungsten coating showed local cracks by 300 cycles but did not induce failure by further cycles. However, the failure of pure tungsten and VPS-tungsten coating by fatigue cracking was observed under higher heat load (55-60 MW/m2) for 420 and 230 cycles, respectively.

本文言語英語
ページ(範囲)687-691
ページ数5
ジャーナルJournal of Nuclear Materials
329-333
1-3 PART A
DOI
出版ステータス出版済み - 8 1 2004
イベントProceedings of the 11th Conference on Fusion Research - Kyoto, 日本
継続期間: 12 7 200312 12 2003

All Science Journal Classification (ASJC) codes

  • 核物理学および高エネルギー物理学
  • 材料科学(全般)
  • 原子力エネルギーおよび原子力工学

フィンガープリント

「High heat flux properties of pure tungsten and plasma sprayed tungsten coatings」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル