A preparation of La0.6Sr0.4Ti0.3Fe 0.7O3 (LSTF) perovskite oxide on a support with a unique multichannel structure achieved a high oxygen permeation rate. A LSTF thin membrane with 60μm thickness was successfully prepared on the multichannel support with 30% porosity. The oxygen permeation rate was much improved by using the multichannel structured support, as the permeated oxygen was removed rapidly. On the other hand, partial oxidation of CH4 into CO and H2 is dominant on the LSTF membrane. The oxygen permeation rate increased as the thickness of the membrane and the porous support decreased, and a value of 13.3 cm3/(min cm2) was achieved at 1273 K under a CH4 partial oxidation condition.