High-resolution transmission electron microscopy analysis of bulk nanograined silicon processed by high-pressure torsion

Yuta Fukushima, Yoshifumi Ikoma, Kaveh Edalati, Bumsoo Chon, David J. Smith, Zenji Horita

研究成果: Contribution to journalArticle査読

13 被引用数 (Scopus)

抄録

We report on high-resolution transmission electron microscopy observations of bulk nanograined silicon processed by severe plastic deformation through high-pressure torsion (HPT). Single crystalline Si(100) was subjected to HPT processing under a nominal pressure of 24 GPa at room temperature. The HPT-processed samples contained lattice defects such as dislocations and nanotwins in diamond-cubic Si-I, and metastable phases such as body-centered-cubic Si-III and hexagonal-diamond Si-IV. The grain size ranged from several nanometers up to several tens of nanometers. Subsequent annealing at 873 K led to the phase transformation to Si-I. No appreciable grain coarsening occurred after annealing while dislocations and nanotwins remained in the Si-I nanograins. The Si-I nanograin structure was retained even after annealing for 12 h.
本文言語英語
ページ(範囲)163–168
ジャーナルMaterials Characterization
129
出版ステータス出版済み - 7 2017

フィンガープリント 「High-resolution transmission electron microscopy analysis of bulk nanograined silicon processed by high-pressure torsion」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル