High-velocity impact damage in CFRP unidirectional and cross-ply laminates

Keiji Ogi, Takaaki Tanaka, Shigeki Yashiro, Akinori Yoshimura

研究成果: Contribution to journalArticle査読

1 被引用数 (Scopus)

抄録

This paper aims at characterizing the high-velocity impact damage behavior in carbon fiber reinforced plastic (CFRP) unidirectional (UD) and cross-ply (CP) laminates. First, the surface and internal damages of CFRP plates impacted at a velocity of 200 and 430m/s were observed by using optical microscopy together with radiography. Next, dynamic finite element analysis was performed to simulate the damage process. Cohesive elements were introduced to express the delamination and splitting cracks while the maximum stress fracture criteria were employed to express the intralaminar failure. Finally, the simulations were compared with the experiment results to verify the reasonability of the analysis. The damage process in both laminates was as follows : 1. A crater accompanied by splitting cracks is generated at the impact point on the front surface while splitting cracks due to bending are observed on the back surface. 2. Cone-shaped matrix cracking is observed in the UD laminate while few matrix cracking is generated in the CP laminate. 3. The shape of the delamination in the UD and CP laminates is a galaxy and a circle, respectively. Delamination size is larger in the CP laminate than in the UD laminate, which results in higher energy absorption capability in the CP laminate. Simulations are in qualitatively good agreement with the experiment results.

本文言語英語
ページ(範囲)418-424
ページ数7
ジャーナルZairyo/Journal of the Society of Materials Science, Japan
60
5
DOI
出版ステータス出版済み - 5 2011
外部発表はい

All Science Journal Classification (ASJC) codes

  • 材料科学(全般)
  • 凝縮系物理学
  • 材料力学
  • 機械工学

フィンガープリント

「High-velocity impact damage in CFRP unidirectional and cross-ply laminates」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル