T1 - Hydrogen, as an alloying element, enables a greater strength-ductility balance in an Fe-Cr-Ni-based, stable austenitic stainless steel
AU - Ogawa, Yuhei
AU - Hosoi, Hyuga
AU - Tsuzaki, Kaneaki
AU - Redarce, Timothée
AU - Takakuwa, Osamu
AU - Matsunaga, Hisao
PY - 2020/10/15
Y1 - 2020/10/15
N2 - After pre-charging at the gaseous phase with a concentration of ~7,000 at. ppm, solute hydrogen was discovered to have an abnormal effect on both the strength and ductility enhancement of a commercially-available, Fe-24Cr-19Ni-based, stable austenitic stainless steel that had been subjected to tensile testing at various strain-rates. Specifically, the impact of hydrogen on material strength was accompanied by amplified yield and flow stresses, as well as tensile strength, while the improvement in ductility featured extended uniform elongation and strain-to-fracture, both of which became more pronounced as hydrogen concentration intensified. The product between tensile strength and uniform elongation served as indicators of the strength-ductility balance, at which hydrogen maximally optimized the indicator at the particular intermediate strain-rate. The yield/flow stress augmentations were interpreted in terms of solid-solution strengthening, whereas the enhanced ductility was primarily ascribed to the facilitation of mechanical twinning, whereby dynamic hydrogen-dislocation interaction exerted a critical influence as was indirectly revealed by supplemental stress-relaxation experiments.
AB - After pre-charging at the gaseous phase with a concentration of ~7,000 at. ppm, solute hydrogen was discovered to have an abnormal effect on both the strength and ductility enhancement of a commercially-available, Fe-24Cr-19Ni-based, stable austenitic stainless steel that had been subjected to tensile testing at various strain-rates. Specifically, the impact of hydrogen on material strength was accompanied by amplified yield and flow stresses, as well as tensile strength, while the improvement in ductility featured extended uniform elongation and strain-to-fracture, both of which became more pronounced as hydrogen concentration intensified. The product between tensile strength and uniform elongation served as indicators of the strength-ductility balance, at which hydrogen maximally optimized the indicator at the particular intermediate strain-rate. The yield/flow stress augmentations were interpreted in terms of solid-solution strengthening, whereas the enhanced ductility was primarily ascribed to the facilitation of mechanical twinning, whereby dynamic hydrogen-dislocation interaction exerted a critical influence as was indirectly revealed by supplemental stress-relaxation experiments.
UR - http://www.scopus.com/inward/record.url?scp=85089809380&partnerID=8YFLogxK
UR - http://www.scopus.com/inward/citedby.url?scp=85089809380&partnerID=8YFLogxK
U2 - 10.1016/j.actamat.2020.08.024
DO - 10.1016/j.actamat.2020.08.024
M3 - Article
AN - SCOPUS:85089809380
VL - 199
SP - 181
EP - 192
JO - Acta Materialia
JF - Acta Materialia
SN - 1359-6454
ER -