Hydrogen embrittlement in a Fe-Mn-C ternary twinning-induced plasticity steel

Motomichi Koyama; Eiji Akiyama; Kaneaki Tsuzaki

doi:10.1016/j.corsci.2011.09.022

Hydrogen embrittlement in a Fe-Mn-C ternary twinning-induced plasticity steel

Motomichi Koyama, Eiji Akiyama, Kaneaki Tsuzaki

研究成果: ジャーナルへの寄稿 › レター › 査読

124 被引用数 (Scopus)

抄録

The influence of hydrogen entry on ductility was evaluated in a ternary twinning-induced plasticity (TWIP) steel with a composition of Fe-18Mn-0.6C in wt.% using tensile tests. The samples with a thickness of 1.2. mm were charged with hydrogen galvanostatically during the tensile tests. Significant hydrogen content was introduced by the hydrogen-charging. The total elongation was significantly deteriorated from approx. 60% to 30% by the hydrogen-charging. A clear intergranular fracture surface was observed in a vicinity of the sample surface in the hydrogen-charged samples.

本文言語	英語
ページ（範囲）	1-4
ページ数	4
ジャーナル	Corrosion Science
巻	54
号	1
DOI	https://doi.org/10.1016/j.corsci.2011.09.022
出版ステータス	出版済み - 1月 2012
外部発表	はい

!!!All Science Journal Classification (ASJC) codes

化学 (全般)
化学工学（全般）
材料科学（全般）

文献へのアクセス

10.1016/j.corsci.2011.09.022

他のファイルとリンク

引用スタイル

@article{3e53c1e8933b466b9f14856114102ab8,

title = "Hydrogen embrittlement in a Fe-Mn-C ternary twinning-induced plasticity steel",

abstract = "The influence of hydrogen entry on ductility was evaluated in a ternary twinning-induced plasticity (TWIP) steel with a composition of Fe-18Mn-0.6C in wt.% using tensile tests. The samples with a thickness of 1.2. mm were charged with hydrogen galvanostatically during the tensile tests. Significant hydrogen content was introduced by the hydrogen-charging. The total elongation was significantly deteriorated from approx. 60% to 30% by the hydrogen-charging. A clear intergranular fracture surface was observed in a vicinity of the sample surface in the hydrogen-charged samples.",

author = "Motomichi Koyama and Eiji Akiyama and Kaneaki Tsuzaki",

note = "Funding Information: M. Koyama acknowledges the Research Fellowship of the Japan Society for the Promotion of Science for Young Scientists. We would also like to acknowledge Dr. Takahiro Sawaguchi for taking part in the discussions during the experiments. POSCO supported this work through providing the samples and funding under a Contract No. ( 22-4119 ). ",

year = "2012",

month = jan,

doi = "10.1016/j.corsci.2011.09.022",

language = "English",

volume = "54",

pages = "1--4",

journal = "Corrosion Science",

issn = "0010-938X",

publisher = "Elsevier Limited",

number = "1",

}

TY - JOUR

T1 - Hydrogen embrittlement in a Fe-Mn-C ternary twinning-induced plasticity steel

AU - Koyama, Motomichi

AU - Akiyama, Eiji

AU - Tsuzaki, Kaneaki

N1 - Funding Information: M. Koyama acknowledges the Research Fellowship of the Japan Society for the Promotion of Science for Young Scientists. We would also like to acknowledge Dr. Takahiro Sawaguchi for taking part in the discussions during the experiments. POSCO supported this work through providing the samples and funding under a Contract No. ( 22-4119 ).

PY - 2012/1

Y1 - 2012/1

N2 - The influence of hydrogen entry on ductility was evaluated in a ternary twinning-induced plasticity (TWIP) steel with a composition of Fe-18Mn-0.6C in wt.% using tensile tests. The samples with a thickness of 1.2. mm were charged with hydrogen galvanostatically during the tensile tests. Significant hydrogen content was introduced by the hydrogen-charging. The total elongation was significantly deteriorated from approx. 60% to 30% by the hydrogen-charging. A clear intergranular fracture surface was observed in a vicinity of the sample surface in the hydrogen-charged samples.

AB - The influence of hydrogen entry on ductility was evaluated in a ternary twinning-induced plasticity (TWIP) steel with a composition of Fe-18Mn-0.6C in wt.% using tensile tests. The samples with a thickness of 1.2. mm were charged with hydrogen galvanostatically during the tensile tests. Significant hydrogen content was introduced by the hydrogen-charging. The total elongation was significantly deteriorated from approx. 60% to 30% by the hydrogen-charging. A clear intergranular fracture surface was observed in a vicinity of the sample surface in the hydrogen-charged samples.

UR - http://www.scopus.com/inward/record.url?scp=80655124519&partnerID=8YFLogxK

UR - http://www.scopus.com/inward/citedby.url?scp=80655124519&partnerID=8YFLogxK

U2 - 10.1016/j.corsci.2011.09.022

DO - 10.1016/j.corsci.2011.09.022

M3 - Letter

AN - SCOPUS:80655124519

SN - 0010-938X

VL - 54

SP - 1

EP - 4

JO - Corrosion Science

JF - Corrosion Science

IS - 1

ER -

Hydrogen embrittlement in a Fe-Mn-C ternary twinning-induced plasticity steel

抄録

!!!All Science Journal Classification (ASJC) codes

文献へのアクセス

他のファイルとリンク

フィンガープリント

引用スタイル