Hydrogen embrittlement in Al-added twinning-induced plasticity steels evaluated by tensile tests during hydrogen charging

Motomichi Koyama, Eiji Akiyama, Kaneaki Tsuzaki

研究成果: Contribution to journalArticle査読

抄録

Hydrogen embrittlement of a Fe-18Mn-0.6C-1.5Al steel was observed in tensile deformation during cathodic hydrogen charging. The fracture mode was quasi-cleavage fracture. The relationship between diffusible hydrogen content and fracture stress was arranged by the power law like that for ferritic and Al-free TWIP steels. The Al addition did not affect the magnitude of the degradation of hydrogen embrittlement property at the same current density in TWIP steels. However, the Al-added steel showed a suppression of hydrogen entry and a larger total elongation in comparison to those of the Al-free TWIP steel in the same environment, although the Al addition decreased fracture stress. The larger elongation is one of the reasons for why the Al addition improves the hydrogen embrittlement property of cup specimens.

本文言語英語
ページ(範囲)662-667
ページ数6
ジャーナルTetsu-To-Hagane/Journal of the Iron and Steel Institute of Japan
100
5
DOI
出版ステータス出版済み - 2014

All Science Journal Classification (ASJC) codes

  • 凝縮系物理学
  • 物理化学および理論化学
  • 金属および合金
  • 材料化学

フィンガープリント

「Hydrogen embrittlement in Al-added twinning-induced plasticity steels evaluated by tensile tests during hydrogen charging」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル