Hydrogen-induced delayed fracture of a martensitic steel with fine prior-austenite grain size

Y. Kimura, S. Takagi, T. Hara, S. Terasaki, K. Tsuzaki

研究成果: Contribution to journalConference article査読

9 被引用数 (Scopus)

抄録

The influence of the grain size of the prior-austenite on the hydrogen-induced delayed fracture property was investigated for a medium carbon tempered martensitic steel (JIS-SCM440) with a tensile strength of 1400MPa. Thermomechanical treatment, which consists of a warm working at 873K by multi-pass bar rolling of tempered martensite and subsequent rapid austenitizing at 1093K for 1s, resulted in the refinement of the prior-austenite grain to 3 μm. The hydrogen embrittlement susceptibility was examined using a conventional creep test machine under a constant load for hydrogen pre-charged notched specimens with a stress concentration factor of 4.9. The critical diffusible hydrogen content, below which the specimen never fracture, was approximately 0.24 mass ppm for the fine-grained specimen under an applied stress of 0.9TS, two times higher than that of the conventional QT sample (prior-austenite grain size; 17 μm). The immersion test in 0.1M HCl water solution (pH=1.0) at 298K showed that the intruded hydrogen content (HE) at 100h was 0.14 mass ppm for the fine-grained sample which was almost the same as that of the conventional QT sample (0.17 mass ppm).

本文言語英語
ページ(範囲)403-406
ページ数4
ジャーナルJournal De Physique. IV : JP
112 I
DOI
出版ステータス出版済み - 10 2003
イベントInternational Conference on Martensitic Transformations - Espoo, フィンランド
継続期間: 6 10 20026 14 2002

All Science Journal Classification (ASJC) codes

  • Physics and Astronomy(all)

フィンガープリント 「Hydrogen-induced delayed fracture of a martensitic steel with fine prior-austenite grain size」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル