Hydrothermal synthesis of mesoporous TiO2-SiO2 core-shell composites for dye-sensitized solar cells

Hui Tong, Naoya Enomoto, Miki Inada, Yumi Tanaka, Junichi Hojo

研究成果: Contribution to journalArticle

11 引用 (Scopus)

抜粋

It is challenging to utilize TiO2-based composites with high specific surface area to improve dye-sensitized solar cells (DSSCs) performance. Herein, we report efficient TiO2-SiO2 core-shell composites for DSSCs by optimizing the microstructure and crystalline structure. Mesoporous TiO2-SiO2 core-shell composites were synthesized by hydrolysis of TiOCl2 and Si(C2H 5O)4 under hydrothermal condition. The shell thickness can be tuned through adjustment of the SiO2 addition content. Rutile phase of TiO2 formed without SiO2 addition, while anatase phase of TiO2 was stabilized by SiO2 loading. By addition of SiO2, the crystallite size decreased from 29 nm of rutile to 15 nm of anatase, and the specific surface area increased from 23 m2/g to 150 m2/g. The best transfer efficiency (5.9%) was obtained in TiO2-SiO2(0.10), which is much higher than that of commercial TiO2 powder (P25).

元の言語英語
ページ(範囲)329-334
ページ数6
ジャーナルElectrochimica Acta
130
DOI
出版物ステータス出版済み - 6 1 2014

All Science Journal Classification (ASJC) codes

  • Chemical Engineering(all)
  • Electrochemistry

フィンガープリント Hydrothermal synthesis of mesoporous TiO<sub>2</sub>-SiO<sub>2</sub> core-shell composites for dye-sensitized solar cells' の研究トピックを掘り下げます。これらはともに一意のフィンガープリントを構成します。

  • これを引用