Improvement of surface densificaron and fatigue strength by tooth root rolling of sintered ferrous alloy gear added Mo

Shigeru Unami, Takuya Goushi, Kentaro Kudo, Fujio Tsumori, Hyung Goo Kang, Hideshi Miura

研究成果: Contribution to journalArticle査読

2 被引用数 (Scopus)

抄録

Surface rolling were carried out using P/M spur gears of 0.6Mo-0.2C partially alloyed sintered steel with the density of 7.18 g/cm 3. A CNC form rolling machine of axis intersection type was employed, and an unmodified screw-shaped rolling tool was prepared. Then, porosity distributions in the surface layer of rolled gear teeth root were measured and the effects of the surface rolling on the selective surface densification behaviors were evaluated. Moreover, to obtain higher fatigue strength, reverse rolling was introduced to standard gears. As a result, the porosities in the tooth root were sufficiently reduced at 700/μm feed in rolling process. Furthermore, a profile shifted gear was prepared to increase the effect of surface rolling. After case hardening, the single tooth bending fatigue durability reached to about 83% of the case hardened wrought steel gears of SCM415.

本文言語英語
ページ(範囲)692-696
ページ数5
ジャーナルFuntai Oyobi Fummatsu Yakin/Journal of the Japan Society of Powder and Powder Metallurgy
58
11
DOI
出版ステータス出版済み - 11 2011

All Science Journal Classification (ASJC) codes

  • Mechanical Engineering
  • Industrial and Manufacturing Engineering
  • Metals and Alloys
  • Materials Chemistry

フィンガープリント 「Improvement of surface densificaron and fatigue strength by tooth root rolling of sintered ferrous alloy gear added Mo」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル