Improvement on out-of-plane impact resistance of CFRP laminates due to through-the-thickness stitching

Akinori Yoshimura, Tomoaki Nakao, Shigeki Yashiro, Nobuo Takeda

研究成果: ジャーナルへの寄稿記事

47 引用 (Scopus)

抄録

The present study both experimentally and numerically investigated the damage process in the stitched laminates under the low velocity impact loading, and revealed the characteristic of the improvement on out-of-plane impact resistance due to stitching. First, we performed drop-weight impact tests and inspected the damage by using non-destructive inspection techniques. We then conducted damage extension simulation using a layer-wise finite element model with stitch threads as beam elements, in which the damage (ply cracks and delamination) was represented by cohesive elements. A detailed comparison between the experimental and simulated results revealed that impact damage resistance was improved more effectively when the impact energy was larger. The simulated results demonstrated that the increase of the number of stitch threads which located inside and near the delamination area caused this phenomenon.

元の言語英語
ページ(範囲)1370-1379
ページ数10
ジャーナルComposites Part A: Applied Science and Manufacturing
39
発行部数9
DOI
出版物ステータス出版済み - 9 1 2008
外部発表Yes

Fingerprint

Impact resistance
Carbon fiber reinforced plastics
Delamination
Laminates
Inspection
Cracks
carbon fiber reinforced plastic

All Science Journal Classification (ASJC) codes

  • Ceramics and Composites
  • Mechanics of Materials

これを引用

Improvement on out-of-plane impact resistance of CFRP laminates due to through-the-thickness stitching. / Yoshimura, Akinori; Nakao, Tomoaki; Yashiro, Shigeki; Takeda, Nobuo.

:: Composites Part A: Applied Science and Manufacturing, 巻 39, 番号 9, 01.09.2008, p. 1370-1379.

研究成果: ジャーナルへの寄稿記事

@article{f2ecc68159364460a4a93c2e0eac7264,
title = "Improvement on out-of-plane impact resistance of CFRP laminates due to through-the-thickness stitching",
abstract = "The present study both experimentally and numerically investigated the damage process in the stitched laminates under the low velocity impact loading, and revealed the characteristic of the improvement on out-of-plane impact resistance due to stitching. First, we performed drop-weight impact tests and inspected the damage by using non-destructive inspection techniques. We then conducted damage extension simulation using a layer-wise finite element model with stitch threads as beam elements, in which the damage (ply cracks and delamination) was represented by cohesive elements. A detailed comparison between the experimental and simulated results revealed that impact damage resistance was improved more effectively when the impact energy was larger. The simulated results demonstrated that the increase of the number of stitch threads which located inside and near the delamination area caused this phenomenon.",
author = "Akinori Yoshimura and Tomoaki Nakao and Shigeki Yashiro and Nobuo Takeda",
year = "2008",
month = "9",
day = "1",
doi = "10.1016/j.compositesa.2008.04.019",
language = "English",
volume = "39",
pages = "1370--1379",
journal = "Composites - Part A: Applied Science and Manufacturing",
issn = "1359-835X",
publisher = "Elsevier Limited",
number = "9",

}

TY - JOUR

T1 - Improvement on out-of-plane impact resistance of CFRP laminates due to through-the-thickness stitching

AU - Yoshimura, Akinori

AU - Nakao, Tomoaki

AU - Yashiro, Shigeki

AU - Takeda, Nobuo

PY - 2008/9/1

Y1 - 2008/9/1

N2 - The present study both experimentally and numerically investigated the damage process in the stitched laminates under the low velocity impact loading, and revealed the characteristic of the improvement on out-of-plane impact resistance due to stitching. First, we performed drop-weight impact tests and inspected the damage by using non-destructive inspection techniques. We then conducted damage extension simulation using a layer-wise finite element model with stitch threads as beam elements, in which the damage (ply cracks and delamination) was represented by cohesive elements. A detailed comparison between the experimental and simulated results revealed that impact damage resistance was improved more effectively when the impact energy was larger. The simulated results demonstrated that the increase of the number of stitch threads which located inside and near the delamination area caused this phenomenon.

AB - The present study both experimentally and numerically investigated the damage process in the stitched laminates under the low velocity impact loading, and revealed the characteristic of the improvement on out-of-plane impact resistance due to stitching. First, we performed drop-weight impact tests and inspected the damage by using non-destructive inspection techniques. We then conducted damage extension simulation using a layer-wise finite element model with stitch threads as beam elements, in which the damage (ply cracks and delamination) was represented by cohesive elements. A detailed comparison between the experimental and simulated results revealed that impact damage resistance was improved more effectively when the impact energy was larger. The simulated results demonstrated that the increase of the number of stitch threads which located inside and near the delamination area caused this phenomenon.

UR - http://www.scopus.com/inward/record.url?scp=50049128131&partnerID=8YFLogxK

UR - http://www.scopus.com/inward/citedby.url?scp=50049128131&partnerID=8YFLogxK

U2 - 10.1016/j.compositesa.2008.04.019

DO - 10.1016/j.compositesa.2008.04.019

M3 - Article

AN - SCOPUS:50049128131

VL - 39

SP - 1370

EP - 1379

JO - Composites - Part A: Applied Science and Manufacturing

JF - Composites - Part A: Applied Science and Manufacturing

SN - 1359-835X

IS - 9

ER -