In situ observation of austenite coarsening induced by massive-like transformation during solidification in Fe-C alloys

H. Yasuda, T. Suga, K. Ichida, T. Narumi, K. Morishita

研究成果: Contribution to journalConference article査読

抄録

A massive-like transformation, in which δ-ferrite massively transforms to γ-austenite in the solid state, was examined by time-resolved X-ray imaging and X-ray diffractometry on a four-dimensional-computed tomography setup. In the unidirectional solidification of a hyperperitectic steel (0.3 mass% C) at 50 μm/s, δ dendrites, fine γ grains that are produced through the massive-like transformation, and coarse γ grains grow together in the steady state. The massive-like transformation occurred commonly in Fe-based alloys with a peritectic reaction in equilibrium. Time-resolved X-ray diffraction measurements for a peritectic steel (0.18 mass% C) showed that the massive-like transformation induced strains in the γ grains. The fine γ grains coarsened and/or vanished and new γ grains formed. The induced strains were released during coarsening. The results obtained by the observations contribute to building of a physical model for γ grain coarsening.

本文言語英語
論文番号012051
ジャーナルIOP Conference Series: Materials Science and Engineering
861
1
DOI
出版ステータス出版済み - 6 12 2020
イベント15th International Conference on Modelling of Casting, Welding and Advanced Solidification Processes, MCWASP 2020 - Jonkoping, スウェーデン
継続期間: 6 22 20206 23 2020