In Situ Observation of Crystal Grain Orientation During Scuffing Process of Steel Surface Using Synchrotron X-ray Diffraction

K. Yagi, T. Izumi, J. Koyamachi, S. Sanda, S. Yamaguchi, K. Satio, M. Tohyama, J. Sugimura

研究成果: Contribution to journalArticle査読

2 被引用数 (Scopus)

抄録

Abstract: Scuffing is a catastrophic failure that causes significant surface damages such as plastic flow and welding with a marked increase in friction, wear, temperature and noise. In this study, variations in the crystal grain structure of a steel surface was analysed in situ during the scuffing process using a synchrotron X-ray diffraction system, combined with a visible camera and a near-infrared thermometer. The in situ observation system was synchronously operated to capture a contact area between a rotating sapphire ring and a stationary bearing steel pin. The Debye–Scherrer ring diffracted from the contact area was captured by a two-dimensional detector. The scuffing behaviour could be classified as either micro scuffing or macro scuffing. During the micro scuffing period, plastic flow occurred intermittently with a significant temperature rise of approximately 1000 °C. During the macro scuffing period, heat was continuously generated over the contact area. When plastic flow occurred, the captured Debye–Scherrer ring indicated the orientation of crystal grains as well as a phase transformation from martensite to austenite. This study constitutes the first in-situ observation of the behaviour of crystal grains in the dynamic recrystallisation process occurring during the scuffing process. Graphic Abstract: [Figure not available: see fulltext.]

本文言語英語
論文番号115
ジャーナルTribology Letters
68
4
DOI
出版ステータス出版済み - 12 1 2020

All Science Journal Classification (ASJC) codes

  • 材料力学
  • 機械工学
  • 表面および界面
  • 表面、皮膜および薄膜

フィンガープリント

「In Situ Observation of Crystal Grain Orientation During Scuffing Process of Steel Surface Using Synchrotron X-ray Diffraction」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル