In-situ SEM study on damage evolution at coarse secondary particles in 6061 aluminum alloy

Hiroyuki Toda, T. Kobayashi, A. Hoshiyama, A. Takahashi

研究成果: ジャーナルへの寄稿記事

4 引用 (Scopus)

抄録

In-situ SEM observations of fracture toughness tests have been used to characterize microscopic damage evolution at coarse particles around a main crack in a 6061 aluminum alloy. About 13% of the particles coarser than 1 μm in diameter is identified as Mg2Si and the remaining is α-AlFeSi. All of the coarse Mg2Si particles suffer from damage within several hundred micrometers from a crack-tip. Meanwhile, some of the α-AlFeSi particles remain intact. The coarser the particles, the more considerably they are damaged. Fracture of the particles is predominantly observed for the coarser particles, while the tendency of interfacial debonding increases with decreases in the particle size. In addition, in-situ fracture strength values of the two kinds of particles are estimated as a function of particle size. Stronger dependency of the strength on the size is shown in the α-AlFeSi particles than in the Mg2Si particles. It is concluded that the fracture toughness of the alloy is scarcely affected by the damage at the coarse particles. However, much more considerable effects on strength and ductility are predicted due to the very low strengths of the particles.

元の言語英語
ページ(範囲)113-118
ページ数6
ジャーナルKeikinzoku/Journal of Japan Institute of Light Metals
51
発行部数2
DOI
出版物ステータス出版済み - 1 1 2001
外部発表Yes

Fingerprint

Fracture toughness
Aluminum alloys
Scanning electron microscopy
Particle size
Debonding
Crack tips
Ductility
Cracks

All Science Journal Classification (ASJC) codes

  • Mechanics of Materials
  • Mechanical Engineering
  • Metals and Alloys
  • Materials Chemistry

これを引用

In-situ SEM study on damage evolution at coarse secondary particles in 6061 aluminum alloy. / Toda, Hiroyuki; Kobayashi, T.; Hoshiyama, A.; Takahashi, A.

:: Keikinzoku/Journal of Japan Institute of Light Metals, 巻 51, 番号 2, 01.01.2001, p. 113-118.

研究成果: ジャーナルへの寄稿記事

@article{b108e6361f6a4f7a912ec37a25334aeb,
title = "In-situ SEM study on damage evolution at coarse secondary particles in 6061 aluminum alloy",
abstract = "In-situ SEM observations of fracture toughness tests have been used to characterize microscopic damage evolution at coarse particles around a main crack in a 6061 aluminum alloy. About 13{\%} of the particles coarser than 1 μm in diameter is identified as Mg2Si and the remaining is α-AlFeSi. All of the coarse Mg2Si particles suffer from damage within several hundred micrometers from a crack-tip. Meanwhile, some of the α-AlFeSi particles remain intact. The coarser the particles, the more considerably they are damaged. Fracture of the particles is predominantly observed for the coarser particles, while the tendency of interfacial debonding increases with decreases in the particle size. In addition, in-situ fracture strength values of the two kinds of particles are estimated as a function of particle size. Stronger dependency of the strength on the size is shown in the α-AlFeSi particles than in the Mg2Si particles. It is concluded that the fracture toughness of the alloy is scarcely affected by the damage at the coarse particles. However, much more considerable effects on strength and ductility are predicted due to the very low strengths of the particles.",
author = "Hiroyuki Toda and T. Kobayashi and A. Hoshiyama and A. Takahashi",
year = "2001",
month = "1",
day = "1",
doi = "10.2464/jilm.51.113",
language = "English",
volume = "51",
pages = "113--118",
journal = "Keikinzoku/Journal of Japan Institute of Light Metals",
issn = "0451-5994",
publisher = "Keikinzoku Gakkai/Japan Institute of Light Metals",
number = "2",

}

TY - JOUR

T1 - In-situ SEM study on damage evolution at coarse secondary particles in 6061 aluminum alloy

AU - Toda, Hiroyuki

AU - Kobayashi, T.

AU - Hoshiyama, A.

AU - Takahashi, A.

PY - 2001/1/1

Y1 - 2001/1/1

N2 - In-situ SEM observations of fracture toughness tests have been used to characterize microscopic damage evolution at coarse particles around a main crack in a 6061 aluminum alloy. About 13% of the particles coarser than 1 μm in diameter is identified as Mg2Si and the remaining is α-AlFeSi. All of the coarse Mg2Si particles suffer from damage within several hundred micrometers from a crack-tip. Meanwhile, some of the α-AlFeSi particles remain intact. The coarser the particles, the more considerably they are damaged. Fracture of the particles is predominantly observed for the coarser particles, while the tendency of interfacial debonding increases with decreases in the particle size. In addition, in-situ fracture strength values of the two kinds of particles are estimated as a function of particle size. Stronger dependency of the strength on the size is shown in the α-AlFeSi particles than in the Mg2Si particles. It is concluded that the fracture toughness of the alloy is scarcely affected by the damage at the coarse particles. However, much more considerable effects on strength and ductility are predicted due to the very low strengths of the particles.

AB - In-situ SEM observations of fracture toughness tests have been used to characterize microscopic damage evolution at coarse particles around a main crack in a 6061 aluminum alloy. About 13% of the particles coarser than 1 μm in diameter is identified as Mg2Si and the remaining is α-AlFeSi. All of the coarse Mg2Si particles suffer from damage within several hundred micrometers from a crack-tip. Meanwhile, some of the α-AlFeSi particles remain intact. The coarser the particles, the more considerably they are damaged. Fracture of the particles is predominantly observed for the coarser particles, while the tendency of interfacial debonding increases with decreases in the particle size. In addition, in-situ fracture strength values of the two kinds of particles are estimated as a function of particle size. Stronger dependency of the strength on the size is shown in the α-AlFeSi particles than in the Mg2Si particles. It is concluded that the fracture toughness of the alloy is scarcely affected by the damage at the coarse particles. However, much more considerable effects on strength and ductility are predicted due to the very low strengths of the particles.

UR - http://www.scopus.com/inward/record.url?scp=0035246404&partnerID=8YFLogxK

UR - http://www.scopus.com/inward/citedby.url?scp=0035246404&partnerID=8YFLogxK

U2 - 10.2464/jilm.51.113

DO - 10.2464/jilm.51.113

M3 - Article

AN - SCOPUS:0035246404

VL - 51

SP - 113

EP - 118

JO - Keikinzoku/Journal of Japan Institute of Light Metals

JF - Keikinzoku/Journal of Japan Institute of Light Metals

SN - 0451-5994

IS - 2

ER -