In situ synchrotron X-ray analysis: Application of high-pressure sliding process to Ti allotropic transformation

Zenji Horita, Daisuke Maruno, Yukimasa Ikeda, Takahiro Masuda, Yongpeng Tang, Makoto Arita, Yuji Higo, Yoshinori Tange, Yasuo Ohishi

研究成果: Contribution to journalArticle査読

1 被引用数 (Scopus)

抄録

In this study, severe plastic deformation through high-pressure sliding (HPS) was applied for in situ high-energy X-ray diffraction analysis at SPring-8 in JASRI (Japan Synchrotron Radiation Research Institute). Allotropic transformation of pure Ti was examined in terms of temperatures, pressures and imposed strain using a miniaturized HPS facility. The true pressure applied on the sample was estimated from the peak shift. Peak broadening due to local variation of pressure was reduced using white X-rays. The phase transformation from ¡ phase to ½ phase occurred at a pressure of 34.5 GPa. Straining by the HPS processing was effective to promote the transformation to the ½ phase and to maintain the ½ phase even at ambient pressure. The reverse transformation from ½ phase to ¡ phase occurred at a temperature of 3110°C under ambient pressure, while under higher pressure as 34 GPa, the ½ phase remained stable even at 3170°C covered in this study. It was suggested that the reverse transformation from the ½ phase to the ¡ phase is controlled by thermal energy.

本文言語英語
ページ(範囲)167-176
ページ数10
ジャーナルMaterials Transactions
62
2
DOI
出版ステータス出版済み - 2 1 2021

All Science Journal Classification (ASJC) codes

  • Materials Science(all)
  • Condensed Matter Physics
  • Mechanics of Materials
  • Mechanical Engineering

フィンガープリント 「In situ synchrotron X-ray analysis: Application of high-pressure sliding process to Ti allotropic transformation」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル