In vitro osteoconductivity evaluation of alumina treated hydrothermally in CaCl2 solution

Abdullah Al-Mahmood Tarique, Kanji Tsuru, Michito Maruta, Akari Takeuchi, Shigeki Matsuya, Yoshihiro Terada, Kunio Ishikawa

研究成果: Contribution to journalArticle査読

4 被引用数 (Scopus)

抄録

Alumina (Al2O3) is classified as bioinert materials and thus, no direct bonding to bone was observed when implanted. In the present investigation, possibility of osteoconductive Al2O3 was evaluated based on hydrothermal treatment in calcium chloride (CaCl2) solution. Based on X-ray photoelectron spectroscopy measurement, Ca 2p peaks were detected on Al2O3 after hydrothermal treatment with 10 and 50mmol/L CaCl2 solution at 125°C. The Ca2p peak intensity for Al2O3 treated with 50mmol/L CaCl2 was higher than that treated with 10mmol/L CaCl2. Then, in vitro osteoconductivity screening evaluation was made using simulated body fluid (SBF). After being soaked in SBF for 14 days, calcium phosphate deposition could be observed on Al2O 3 treated with 10 and 50mmol/L CaCl2 solution at 125°C for 7 days whereas no deposition was observed on Al2O3 treated at 150 and 200°C as well as non-treated Al2O3. We concluded, therefore, osteoconductive Al2O3 could be fabricated based on the hydrothermal treatment of bioinert Al2O 3 with CaCl2.

本文言語英語
ページ(範囲)512-515
ページ数4
ジャーナルJournal of the Ceramic Society of Japan
118
1378
DOI
出版ステータス出版済み - 6 2010

All Science Journal Classification (ASJC) codes

  • セラミックおよび複合材料
  • 化学 (全般)
  • 凝縮系物理学
  • 材料化学

フィンガープリント

「In vitro osteoconductivity evaluation of alumina treated hydrothermally in CaCl<sub>2</sub> solution」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル