Influence of cathode polarization change on chromium deposited on electrolyte surface near cathode reaction sites of SOFC

Daiki Ishibashi, Eunjoo Park, Shunsuke Taniguchi, Yuko Inoue, Jyh Tyng Chou, Kazunari Sasaki

研究成果: 著書/レポートタイプへの貢献会議での発言

抄録

It has been clarified that Cr deposition occurs significantly on the electrolyte surface near cathode reaction sites as a consequence of cathode polarization. In this study, we investigated the influence of a change in the cathode polarization on the Cr deposited on the electrolyte surface by using NiO/YSZ or NiO/GDC as the cathode material. The deposited Cr segregated at the interface of NiO and YSZ in the case of the NiO/YSZ cathode after a decrease in the cathode polarization, which suggests nucleation under a cathode polarization of 200 mV and growth of Cr compounds after decreasing the cathode polarization. In contrast, the amount of deposited Cr decreased in the case of the NiO/GDC cathode after decreasing the cathode polarization.

元の言語英語
ホスト出版物のタイトルSolid Oxide Fuel Cells 14, SOFC 2015
編集者K. Eguchi, S. C. Singhal
出版者Electrochemical Society Inc.
ページ1031-1037
ページ数7
エディション1
ISBN(電子版)9781607685395
DOI
出版物ステータス出版済み - 1 1 2015
イベント14th International Symposium on Solid Oxide Fuel Cells, SOFC 2015; held as part of the Electrochemical Society, ECS Conference on Electrochemical Energy Conversion and Storage - Glasgow, 英国
継続期間: 7 26 20157 31 2015

出版物シリーズ

名前ECS Transactions
番号1
68
ISSN(印刷物)1938-5862
ISSN(電子版)1938-6737

その他

その他14th International Symposium on Solid Oxide Fuel Cells, SOFC 2015; held as part of the Electrochemical Society, ECS Conference on Electrochemical Energy Conversion and Storage
英国
Glasgow
期間7/26/157/31/15

Fingerprint

Solid oxide fuel cells (SOFC)
Chromium
Cathodes
Electrolytes
Polarization
Nucleation

All Science Journal Classification (ASJC) codes

  • Engineering(all)

これを引用

Ishibashi, D., Park, E., Taniguchi, S., Inoue, Y., Chou, J. T., & Sasaki, K. (2015). Influence of cathode polarization change on chromium deposited on electrolyte surface near cathode reaction sites of SOFC. : K. Eguchi, & S. C. Singhal (版), Solid Oxide Fuel Cells 14, SOFC 2015 (1 版, pp. 1031-1037). (ECS Transactions; 巻数 68, 番号 1). Electrochemical Society Inc.. https://doi.org/10.1149/06801.1031ecst

Influence of cathode polarization change on chromium deposited on electrolyte surface near cathode reaction sites of SOFC. / Ishibashi, Daiki; Park, Eunjoo; Taniguchi, Shunsuke; Inoue, Yuko; Chou, Jyh Tyng; Sasaki, Kazunari.

Solid Oxide Fuel Cells 14, SOFC 2015. 版 / K. Eguchi; S. C. Singhal. 1. 編 Electrochemical Society Inc., 2015. p. 1031-1037 (ECS Transactions; 巻 68, 番号 1).

研究成果: 著書/レポートタイプへの貢献会議での発言

Ishibashi, D, Park, E, Taniguchi, S, Inoue, Y, Chou, JT & Sasaki, K 2015, Influence of cathode polarization change on chromium deposited on electrolyte surface near cathode reaction sites of SOFC. : K Eguchi & SC Singhal (版), Solid Oxide Fuel Cells 14, SOFC 2015. 1 Edn, ECS Transactions, 番号 1, 巻. 68, Electrochemical Society Inc., pp. 1031-1037, 14th International Symposium on Solid Oxide Fuel Cells, SOFC 2015; held as part of the Electrochemical Society, ECS Conference on Electrochemical Energy Conversion and Storage, Glasgow, 英国, 7/26/15. https://doi.org/10.1149/06801.1031ecst
Ishibashi D, Park E, Taniguchi S, Inoue Y, Chou JT, Sasaki K. Influence of cathode polarization change on chromium deposited on electrolyte surface near cathode reaction sites of SOFC. : Eguchi K, Singhal SC, 編集者, Solid Oxide Fuel Cells 14, SOFC 2015. 1 版 Electrochemical Society Inc. 2015. p. 1031-1037. (ECS Transactions; 1). https://doi.org/10.1149/06801.1031ecst
Ishibashi, Daiki ; Park, Eunjoo ; Taniguchi, Shunsuke ; Inoue, Yuko ; Chou, Jyh Tyng ; Sasaki, Kazunari. / Influence of cathode polarization change on chromium deposited on electrolyte surface near cathode reaction sites of SOFC. Solid Oxide Fuel Cells 14, SOFC 2015. 編集者 / K. Eguchi ; S. C. Singhal. 1. 版 Electrochemical Society Inc., 2015. pp. 1031-1037 (ECS Transactions; 1).
@inproceedings{6fc0b85da9594f4ba121160bbcb84848,
title = "Influence of cathode polarization change on chromium deposited on electrolyte surface near cathode reaction sites of SOFC",
abstract = "It has been clarified that Cr deposition occurs significantly on the electrolyte surface near cathode reaction sites as a consequence of cathode polarization. In this study, we investigated the influence of a change in the cathode polarization on the Cr deposited on the electrolyte surface by using NiO/YSZ or NiO/GDC as the cathode material. The deposited Cr segregated at the interface of NiO and YSZ in the case of the NiO/YSZ cathode after a decrease in the cathode polarization, which suggests nucleation under a cathode polarization of 200 mV and growth of Cr compounds after decreasing the cathode polarization. In contrast, the amount of deposited Cr decreased in the case of the NiO/GDC cathode after decreasing the cathode polarization.",
author = "Daiki Ishibashi and Eunjoo Park and Shunsuke Taniguchi and Yuko Inoue and Chou, {Jyh Tyng} and Kazunari Sasaki",
year = "2015",
month = "1",
day = "1",
doi = "10.1149/06801.1031ecst",
language = "English",
series = "ECS Transactions",
publisher = "Electrochemical Society Inc.",
number = "1",
pages = "1031--1037",
editor = "K. Eguchi and Singhal, {S. C.}",
booktitle = "Solid Oxide Fuel Cells 14, SOFC 2015",
edition = "1",

}

TY - GEN

T1 - Influence of cathode polarization change on chromium deposited on electrolyte surface near cathode reaction sites of SOFC

AU - Ishibashi, Daiki

AU - Park, Eunjoo

AU - Taniguchi, Shunsuke

AU - Inoue, Yuko

AU - Chou, Jyh Tyng

AU - Sasaki, Kazunari

PY - 2015/1/1

Y1 - 2015/1/1

N2 - It has been clarified that Cr deposition occurs significantly on the electrolyte surface near cathode reaction sites as a consequence of cathode polarization. In this study, we investigated the influence of a change in the cathode polarization on the Cr deposited on the electrolyte surface by using NiO/YSZ or NiO/GDC as the cathode material. The deposited Cr segregated at the interface of NiO and YSZ in the case of the NiO/YSZ cathode after a decrease in the cathode polarization, which suggests nucleation under a cathode polarization of 200 mV and growth of Cr compounds after decreasing the cathode polarization. In contrast, the amount of deposited Cr decreased in the case of the NiO/GDC cathode after decreasing the cathode polarization.

AB - It has been clarified that Cr deposition occurs significantly on the electrolyte surface near cathode reaction sites as a consequence of cathode polarization. In this study, we investigated the influence of a change in the cathode polarization on the Cr deposited on the electrolyte surface by using NiO/YSZ or NiO/GDC as the cathode material. The deposited Cr segregated at the interface of NiO and YSZ in the case of the NiO/YSZ cathode after a decrease in the cathode polarization, which suggests nucleation under a cathode polarization of 200 mV and growth of Cr compounds after decreasing the cathode polarization. In contrast, the amount of deposited Cr decreased in the case of the NiO/GDC cathode after decreasing the cathode polarization.

UR - http://www.scopus.com/inward/record.url?scp=84938809574&partnerID=8YFLogxK

UR - http://www.scopus.com/inward/citedby.url?scp=84938809574&partnerID=8YFLogxK

U2 - 10.1149/06801.1031ecst

DO - 10.1149/06801.1031ecst

M3 - Conference contribution

AN - SCOPUS:84938809574

T3 - ECS Transactions

SP - 1031

EP - 1037

BT - Solid Oxide Fuel Cells 14, SOFC 2015

A2 - Eguchi, K.

A2 - Singhal, S. C.

PB - Electrochemical Society Inc.

ER -