Influence of desorption recombination temperatures on microstructure and coercivity of HDDR-processed anisotropic Nd-Fe-B magnet powders

Rina Takizawa, Hiroshi Akamine, Masaru Itakura, Minoru Nishida, Nobuhiro Katayama, Koichiro Morimoto

研究成果: Contribution to journalArticle査読

抄録

In the hydrogenation decomposition desorption recombination(HDDR)processed Nd Fe Co B Al Ga Zr magnet powders, influence of the desorption recombination(DR)temperatures on the microstructures was investigated by high resolution scanning electron microscopy and scanning transmission electron microscopy. By applying the DR treatment under high vacuum(DR Step 2)at relative low temperatures about 973 K, we can obtain the excellent texture in which the average size of Nd2Fe14B grains is refined to about 240 nm and the grain boundary(GB)phase is uniformly dispersed around the Nd2Fe14B grains. In the GB phase, furthermore, the Nd composition increases and the(Fe, Co)composition decreases drastically with decreasing the DR temperatures, and then Nd rich GB phase with more than 65 at.%Nd can be formed at 973 K. At 973 K, however, the region with unformed GB phase is remained about 10% of the specimen, which leads to deterioration of the coercivity. It was found that the gently DR treatment is very effective not only for increasing the coercivity but also for improving the squareness in demagnetization curve.

本文言語英語
ページ(範囲)121-124
ページ数4
ジャーナルNippon Kinzoku Gakkaishi/Journal of the Japan Institute of Metals
82
4
DOI
出版ステータス出版済み - 2018

All Science Journal Classification (ASJC) codes

  • Condensed Matter Physics
  • Mechanics of Materials
  • Metals and Alloys
  • Materials Chemistry

フィンガープリント 「Influence of desorption recombination temperatures on microstructure and coercivity of HDDR-processed anisotropic Nd-Fe-B magnet powders」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル