Influence of discontinuous columnar defects on flux pinning properties in GdBCO coated conductors

Tetsuro Sueyoshi, Tetsuya Kotaki, Yuuichi Furuki, Yuusei Uraguchi, Takafumi Kai, Takanori Fujiyoshi, Yusuke Shimada, Kazuhiro Yasuda, Norito Ishikawa

研究成果: ジャーナルへの寄稿記事

4 引用 (Scopus)

抜粋

To investigate the effect of discontinuity of 1-D pinning centers on the flux pinning in a wide range of magnetic field directions, discontinuous columnar defects (CDs) and continuous CDs were formed in GdBCO coated conductors using Xe-ion irradiations with 80 and 270 MeV, respectively. An overall shift upward in Jc, for the 80-MeV-irradiated sample compared to the 270-MeV-irradiated one, can be observed in every direction of magnetic field, which is more remarkable as temperature decreases. This implies a synergetic effect of the pinning interaction between the linearity and the discontinuity for the discontinuous CDs. When the density of CDs is lower, however, the difference in Jc between the discontinuous and the continuous CDs becomes less at lower temperature, even in the magnetic field parallel to the c-axis. At lower density of CDs, the average spacing between CDs is wider, which would hardly lead to automatic entanglement of flux lines in the discontinuous CDs, i.e., to the synergetic effect.

元の言語英語
記事番号6966747
ジャーナルIEEE Transactions on Applied Superconductivity
25
発行部数3
DOI
出版物ステータス出版済み - 6 1 2015

    フィンガープリント

All Science Journal Classification (ASJC) codes

  • Electronic, Optical and Magnetic Materials
  • Condensed Matter Physics
  • Electrical and Electronic Engineering

これを引用

Sueyoshi, T., Kotaki, T., Furuki, Y., Uraguchi, Y., Kai, T., Fujiyoshi, T., ... Ishikawa, N. (2015). Influence of discontinuous columnar defects on flux pinning properties in GdBCO coated conductors. IEEE Transactions on Applied Superconductivity, 25(3), [6966747]. https://doi.org/10.1109/TASC.2014.2374554