Influence of size and proximity of paint coating defects on corrosion behavior of carbon steel plates

Shigenobu Kainuma, Young Soo Jeong, Junji Kobayashi

研究成果: 著書/レポートタイプへの貢献会議での発言

1 引用 (Scopus)

抄録

To ensure the safety of painted steel structures, it is important to evaluate the influence of the size and proximity of coating defects on corrosion behavior. In this research, accelerated exposure tests were carried out using combined corrosion cycles, which consisted of exposure to atomizing salt water, wetting, and drying with hot and warm wind. The test specimens were paint-coated steel plates with individual circular machined coating defects 1, 3, 10, and 15 mm in diameter. Multi-circular defects 1 mm in diameter were also created in the specimens. The test results indicate that the mean and maximum corrosion depths increased with increasing diameter of the single defect of the coated steel plate. When actual coated steel members are exposed to corrosive chloride environments such as those represented by the corrosion cycle testing conducted in this research, the corrosion depth for multi-circular defects 1 mm in diameter appears to be 1.5 to 2.5 times greater than that for a single-circular defect.

元の言語英語
ホスト出版物のタイトルAdvances in Fracture and Damage Mechanics XIV
編集者Zdenko Tonkovic, Darko Bajic, Ferri Aliabadi
出版者Trans Tech Publications Ltd
ページ125-128
ページ数4
ISBN(印刷物)9783038355410
DOI
出版物ステータス出版済み - 1 1 2016
イベント14th International Conference on Fracture and Damage Mechanics, FDM 2015 - Budva, モンテネグロ
継続期間: 9 21 20159 23 2015

出版物シリーズ

名前Key Engineering Materials
665
ISSN(印刷物)1013-9826

その他

その他14th International Conference on Fracture and Damage Mechanics, FDM 2015
モンテネグロ
Budva
期間9/21/159/23/15

Fingerprint

Paint
Carbon steel
Corrosion
Coatings
Defects
Steel
Caustics
Saline water
Steel structures
Wetting
Chlorides
Drying
Testing

All Science Journal Classification (ASJC) codes

  • Materials Science(all)
  • Mechanics of Materials
  • Mechanical Engineering

これを引用

Kainuma, S., Jeong, Y. S., & Kobayashi, J. (2016). Influence of size and proximity of paint coating defects on corrosion behavior of carbon steel plates. : Z. Tonkovic, D. Bajic, & F. Aliabadi (版), Advances in Fracture and Damage Mechanics XIV (pp. 125-128). (Key Engineering Materials; 巻数 665). Trans Tech Publications Ltd. https://doi.org/10.4028/www.scientific.net/KEM.665.125

Influence of size and proximity of paint coating defects on corrosion behavior of carbon steel plates. / Kainuma, Shigenobu; Jeong, Young Soo; Kobayashi, Junji.

Advances in Fracture and Damage Mechanics XIV. 版 / Zdenko Tonkovic; Darko Bajic; Ferri Aliabadi. Trans Tech Publications Ltd, 2016. p. 125-128 (Key Engineering Materials; 巻 665).

研究成果: 著書/レポートタイプへの貢献会議での発言

Kainuma, S, Jeong, YS & Kobayashi, J 2016, Influence of size and proximity of paint coating defects on corrosion behavior of carbon steel plates. : Z Tonkovic, D Bajic & F Aliabadi (版), Advances in Fracture and Damage Mechanics XIV. Key Engineering Materials, 巻. 665, Trans Tech Publications Ltd, pp. 125-128, 14th International Conference on Fracture and Damage Mechanics, FDM 2015, Budva, モンテネグロ, 9/21/15. https://doi.org/10.4028/www.scientific.net/KEM.665.125
Kainuma S, Jeong YS, Kobayashi J. Influence of size and proximity of paint coating defects on corrosion behavior of carbon steel plates. : Tonkovic Z, Bajic D, Aliabadi F, 編集者, Advances in Fracture and Damage Mechanics XIV. Trans Tech Publications Ltd. 2016. p. 125-128. (Key Engineering Materials). https://doi.org/10.4028/www.scientific.net/KEM.665.125
Kainuma, Shigenobu ; Jeong, Young Soo ; Kobayashi, Junji. / Influence of size and proximity of paint coating defects on corrosion behavior of carbon steel plates. Advances in Fracture and Damage Mechanics XIV. 編集者 / Zdenko Tonkovic ; Darko Bajic ; Ferri Aliabadi. Trans Tech Publications Ltd, 2016. pp. 125-128 (Key Engineering Materials).
@inproceedings{9d9131a2420c4c9a93426503e4338b3a,
title = "Influence of size and proximity of paint coating defects on corrosion behavior of carbon steel plates",
abstract = "To ensure the safety of painted steel structures, it is important to evaluate the influence of the size and proximity of coating defects on corrosion behavior. In this research, accelerated exposure tests were carried out using combined corrosion cycles, which consisted of exposure to atomizing salt water, wetting, and drying with hot and warm wind. The test specimens were paint-coated steel plates with individual circular machined coating defects 1, 3, 10, and 15 mm in diameter. Multi-circular defects 1 mm in diameter were also created in the specimens. The test results indicate that the mean and maximum corrosion depths increased with increasing diameter of the single defect of the coated steel plate. When actual coated steel members are exposed to corrosive chloride environments such as those represented by the corrosion cycle testing conducted in this research, the corrosion depth for multi-circular defects 1 mm in diameter appears to be 1.5 to 2.5 times greater than that for a single-circular defect.",
author = "Shigenobu Kainuma and Jeong, {Young Soo} and Junji Kobayashi",
year = "2016",
month = "1",
day = "1",
doi = "10.4028/www.scientific.net/KEM.665.125",
language = "English",
isbn = "9783038355410",
series = "Key Engineering Materials",
publisher = "Trans Tech Publications Ltd",
pages = "125--128",
editor = "Zdenko Tonkovic and Darko Bajic and Ferri Aliabadi",
booktitle = "Advances in Fracture and Damage Mechanics XIV",

}

TY - GEN

T1 - Influence of size and proximity of paint coating defects on corrosion behavior of carbon steel plates

AU - Kainuma, Shigenobu

AU - Jeong, Young Soo

AU - Kobayashi, Junji

PY - 2016/1/1

Y1 - 2016/1/1

N2 - To ensure the safety of painted steel structures, it is important to evaluate the influence of the size and proximity of coating defects on corrosion behavior. In this research, accelerated exposure tests were carried out using combined corrosion cycles, which consisted of exposure to atomizing salt water, wetting, and drying with hot and warm wind. The test specimens were paint-coated steel plates with individual circular machined coating defects 1, 3, 10, and 15 mm in diameter. Multi-circular defects 1 mm in diameter were also created in the specimens. The test results indicate that the mean and maximum corrosion depths increased with increasing diameter of the single defect of the coated steel plate. When actual coated steel members are exposed to corrosive chloride environments such as those represented by the corrosion cycle testing conducted in this research, the corrosion depth for multi-circular defects 1 mm in diameter appears to be 1.5 to 2.5 times greater than that for a single-circular defect.

AB - To ensure the safety of painted steel structures, it is important to evaluate the influence of the size and proximity of coating defects on corrosion behavior. In this research, accelerated exposure tests were carried out using combined corrosion cycles, which consisted of exposure to atomizing salt water, wetting, and drying with hot and warm wind. The test specimens were paint-coated steel plates with individual circular machined coating defects 1, 3, 10, and 15 mm in diameter. Multi-circular defects 1 mm in diameter were also created in the specimens. The test results indicate that the mean and maximum corrosion depths increased with increasing diameter of the single defect of the coated steel plate. When actual coated steel members are exposed to corrosive chloride environments such as those represented by the corrosion cycle testing conducted in this research, the corrosion depth for multi-circular defects 1 mm in diameter appears to be 1.5 to 2.5 times greater than that for a single-circular defect.

UR - http://www.scopus.com/inward/record.url?scp=84952845283&partnerID=8YFLogxK

UR - http://www.scopus.com/inward/citedby.url?scp=84952845283&partnerID=8YFLogxK

U2 - 10.4028/www.scientific.net/KEM.665.125

DO - 10.4028/www.scientific.net/KEM.665.125

M3 - Conference contribution

AN - SCOPUS:84952845283

SN - 9783038355410

T3 - Key Engineering Materials

SP - 125

EP - 128

BT - Advances in Fracture and Damage Mechanics XIV

A2 - Tonkovic, Zdenko

A2 - Bajic, Darko

A2 - Aliabadi, Ferri

PB - Trans Tech Publications Ltd

ER -