Interpretation of material hardness, stress ratio, and crack size effects on the ΔKth of small cracks based on crack closure measurement

Y. Kondo, C. Sakae, Masanobu Kubota, M. Kashiwagi

    研究成果: Contribution to journalArticle査読

    2 被引用数 (Scopus)

    抄録

    Fatigue tests were performed on materials containing small cracks to investigate the effects of material hardness, mean stress, and crack size on the threshold stress intensity factor of small cracks. The crack closure measurement on a very small crack was done. Although most of those effects could be explained by the characteristic behavior of crack closure in small cracks, it was also shown that (ΔKeff)th was also affected by crack size. The combination of (ΔKeff) th and the crack closure behaviors caused the peculiar characteristics of ΔKth in small cracks. At an extremely high R region, an unusual decrease in ΔKth was found to occur. The large reduction occurred under the conjunction of three factors: extremely high stress ratio higher than 0.8, shallow crack less than a few tenths of a millimeter, and hard material whose HV is higher than 300. The near-threshold fatigue crack propagation rate could be uniquely evaluated even in such a short crack regime using the effective stress intensity factor with the following modification {ΔKeff - (ΔKeff)th,a}. This expression could be applicable in the short crack regime. ΔK eff still plays a role as the governing parameter for fatigue crack propagation of short crack as short as 0.04 mm.

    本文言語英語
    ページ(範囲)69-83
    ページ数15
    ジャーナルJournal of ASTM International
    2
    4
    DOI
    出版ステータス出版済み - 4 1 2005

    All Science Journal Classification (ASJC) codes

    • Environmental Engineering
    • Materials Science(all)
    • Nuclear Energy and Engineering
    • Engineering(all)
    • Public Health, Environmental and Occupational Health

    フィンガープリント 「Interpretation of material hardness, stress ratio, and crack size effects on the ΔK<sub>th</sub> of small cracks based on crack closure measurement」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

    引用スタイル