Ion irradiation-induced amorphization and nano-crystal formation in garnets

S. Utsunomiya, L. M. Wang, S. Yudintsev, R. C. Ewing

研究成果: Contribution to journalArticle査読

39 被引用数 (Scopus)

抄録

The radiation susceptibility of garnet structure types (A3B2(XO4)3, Ia3d, Z = 8) has been examined by 1.0 MeV Kr2+ irradiation with in situ transmission electron microscopy over the temperature range of 50-1070 K. The target garnets included five natural garnets: almandine, andradite, pyrope, grossular and spessartine, and five synthetic garnets incorporating various contents of actinides. The synthetic garnets were silicates (N-series) and ferrate-aluminates (G-series). The critical amorphization temperature (Tc), above which amorphization does not occur, were determined to be 1050 K for N77, 1130 K for N56, 1100 K for G3, 890 K for G4 and 1030 K for andradite. Tc of the synthetic garnets increased with increasing mass density of the target and as the electronic-to-nuclear stopping power ratio decreased. During ion irradiation of the G3 garnet at a temperature of 1023 K near the Tc, nano-crystals were produced in which the unit-cell parameter of the original garnet was halved (∼0.64 nm) as a result of a radiation-induced recrystallization process, without evidence for ordering of the cations.

本文言語英語
ページ(範囲)177-187
ページ数11
ジャーナルJournal of Nuclear Materials
303
2-3
DOI
出版ステータス出版済み - 6 1 2002
外部発表はい

All Science Journal Classification (ASJC) codes

  • Nuclear and High Energy Physics
  • Materials Science(all)
  • Nuclear Energy and Engineering

フィンガープリント 「Ion irradiation-induced amorphization and nano-crystal formation in garnets」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル