Lattice defects in V-Ti BCC alloys before and after hydrogenation

研究成果: Contribution to journalArticle査読

20 被引用数 (Scopus)

抄録

Microstructures of V-Ti BCC alloys before and after hydrogenation/ dehydrogenation are investigated using transmission electron microscopy. Strain contrast with spacing smaller than 20 nm is observed both in the as-cast alloys and hydrogenated alloys. Twin boundaries and stacking faults with spacing of 5-20 nm are introduced into the V-Ti BCC alloys after hydrogenation. These are parallel to {1-1 1} planes of FCC hydrides. The twin boundaries and stacking faults are formed due to the accommodation of shear stress during hydrogenation accompanied by large anisotropic expansion along the c-axis direction in V-Ti BCC alloys. Density of twin boundaries is high in the alloys with small contents of V, which have a small effective hydrogen capacity at ambient condition. Dependence of microstructure evolution in the V-Ti alloys during hydrogenation on the V/Ti ratio is also discussed with the thermodynamic stabilities from measurements of Pressure-Composition isotherms and mechanical properties.

本文言語英語
ページ(範囲)369-372
ページ数4
ジャーナルJournal of Alloys and Compounds
581
DOI
出版ステータス出版済み - 2013

All Science Journal Classification (ASJC) codes

  • 材料力学
  • 機械工学
  • 金属および合金
  • 材料化学

フィンガープリント

「Lattice defects in V-Ti BCC alloys before and after hydrogenation」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル