Lithium Depletion and the Rechargeability of Li-O2 Batteries in Ether and Carbonate Electrolytes

Il Chan Jang, Shintaro Ida, Tatsumi Ishihara

研究成果: ジャーナルへの寄稿記事

14 引用 (Scopus)

抜粋

Li metal is a highly promising candidate anode material because of its high energy density. However, Li depletion caused by the formation of a passivation layer and dendrites prevent the use of Li metal for rechargeable batteries. In this study, we investigate Li depletion in practical Li-O2 batteries by using two typical electrolytes, carbonate and ether, under high Li utilization. The ether-based solvent tetraethylene glycol dimethyl ether (TEGDME) showed greatly increased levels of Li depletion through the formation of both solid electrolyte interphase (SEI) layers and dendrites than carbonated-based solvents (ethylene carbonate/diethyl carbonate (EC/DEC)). Although TEGDME is known as a stable solvent for oxygen reduction species, it may be less appropriate as a solvent with respect to Li reactivity, which is very important for the cycle stability of Li-O2 battery systems. In contrast, although slight decomposition of EC-DEC was observed, cells constructed with EC-DEC were found to be more stable than those with TEGDME for Li-O2 batteries.

元の言語英語
ページ(範囲)1380-1384
ページ数5
ジャーナルChemElectroChem
2
発行部数9
DOI
出版物ステータス出版済み - 9 1 2015

    フィンガープリント

All Science Journal Classification (ASJC) codes

  • Catalysis
  • Electrochemistry

これを引用