Loading frequency effects on the fatigue crack growth rate and fracture surface morphology of low carbon steel in case of long-term use in hydrogen gas

A. Nishimoto, Y. Oda, H. Noguchi

研究成果: 書籍/レポート タイプへの寄稿会議への寄与

抄録

Loading frequency effects on FCGR and fracture surface morphology were investigated on pre-strained low carbon steel in high FCGR range. Loading frequency effects showed the different trend between internal hydrogen and environmental hydrogen. The effects of combined condition hydrogen revealed similar tendency of environmental hydrogen.

本文言語英語
ホスト出版物のタイトルAdvances in Fracture and Damage Mechanics X
出版社Trans Tech Publications Ltd
ページ323-326
ページ数4
ISBN(印刷版)9783037852187
DOI
出版ステータス出版済み - 2012
イベント10th International Conference on Fracture and Damage Mechanics, FDM2011 - Dubrovnik, クロアチア
継続期間: 9月 19 20119月 21 2011

出版物シリーズ

名前Key Engineering Materials
488-489
ISSN(印刷版)1013-9826
ISSN(電子版)1662-9795

その他

その他10th International Conference on Fracture and Damage Mechanics, FDM2011
国/地域クロアチア
CityDubrovnik
Period9/19/119/21/11

!!!All Science Journal Classification (ASJC) codes

  • 材料科学(全般)
  • 材料力学
  • 機械工学

フィンガープリント

「Loading frequency effects on the fatigue crack growth rate and fracture surface morphology of low carbon steel in case of long-term use in hydrogen gas」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル