Low-temperature (∼250°C) gold-induced lateral growth of Sn-doped Ge on insulator enhanced by layer-exchange reaction

Taizoh Sadoh, Takatsugu Sakai, Ryo Matsumura

研究成果: Contribution to journalArticle査読

抄録

Low-temperature (≤250°C) formation of Sn-doped Ge (GeSn) (substitutional Sn concentration: 2-3%) on insulator is desired to realize flexible electronics, where high-speed thin-film transistors are integrated on flexible plastic-substrates (softening temperature: ∼300°C). To achieve this, gold-induced lateral crystallization of amorphous GeSn (a-GeSn) is investigated. Here, a-GeSn (Sn concentration: 0%-20%) on insulator structures, having Au-island patterns, were annealed. For initial Sn concentrations of 0%-5%, high-speed lateral crystallization proceeds around Au-patterns, and large grown regions (∼5-20 μm) are obtained by low-temperature short-time annealing (150°C-250°C, 10 min). However, bottom regions of GeSn are not crystallized at 150°C-200°C, while the whole films including bottom regions are crystallized at 250°C. These phenomena are caused by the following temperature-dependent growth mechanisms. At 150°C-200°C, Au atoms are supplied into surface-regions of a-GeSn films from Au-islands by surface-diffusion, resulting in crystallization of only surface-regions. On the other hand, at 250°C, layer-exchange of Au/GeSn occurs, which increases supply channel of Au for diffusion. This results in complete crystallization of GeSn to the bottom. Substitutional Sn concentrations in grown layers are increased with increasing annealing temperature. As a result, GeSn films (substitutional Sn concentration: ∼3%) are obtained at ∼250°C.

本文言語英語
ページ(範囲)P609-P614
ジャーナルECS Journal of Solid State Science and Technology
8
10
DOI
出版ステータス出版済み - 2019

All Science Journal Classification (ASJC) codes

  • 電子材料、光学材料、および磁性材料

フィンガープリント

「Low-temperature (∼250°C) gold-induced lateral growth of Sn-doped Ge on insulator enhanced by layer-exchange reaction」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル