Luminescent sintered silica glass prepared by adsorbing Pr ions into mesoporous SiO2-PVA nanocomposite

Hiroshi Ikeda, Takahiro Murata, Shigeru Fujino

    研究成果: Contribution to journalArticle査読

    2 被引用数 (Scopus)

    抄録

    A monolithic silica glass doped with Pr3+ was prepared by immersing a mesoporous SiO2-polyvinly alcohol (PVA) nanocomposite in a Pr nitrate solution and then sintering it at 1100°C in air. The sintered glass exhibited pink emission when excited by ultraviolet irradiation. The photoluminescence intensity of the glass depended on the total concentration of Pr ions, which was adjusted by changing the concentration of the Pr nitrate solution and the immersion time. The glass with the highest photoluminescence intensity was prepared by using a 1- or 10-mM Pr solution at an immersion time of 60 min. To reveal how the immersion conditions affected the photoluminescence intensity, we analyzed and discussed the adsorption kinetics of the Pr ions onto the surface of the mesoporous nanocomposite. At immersion times below 60 min, the Pr ions diffused into pores of the nanocomposite without aggregating. To prepare Pr3+-doped silica glass with high photoluminescence, both the concentration of the Pr solution and the immersion time must be controlled.

    本文言語英語
    ページ(範囲)2541-2547
    ページ数7
    ジャーナルJournal of Composite Materials
    50
    18
    DOI
    出版ステータス出版済み - 8 1 2016

    All Science Journal Classification (ASJC) codes

    • Ceramics and Composites
    • Mechanics of Materials
    • Mechanical Engineering
    • Materials Chemistry

    フィンガープリント 「Luminescent sintered silica glass prepared by adsorbing Pr ions into mesoporous SiO<sub>2</sub>-PVA nanocomposite」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

    引用スタイル