Magnetic properties of Sm-Co-Cu and Sm-Co-Cu/Co exchange-spring films with high coercivity

Y. Yamazaki, K. Takano, H. Takamura, S. Sugimoto, M. Homma, M. Okada

研究成果: Contribution to journalArticle査読

3 被引用数 (Scopus)

抄録

The magnetic properties of Sm-Co-Cu films and Sm-Co-Cu/Co multilayered films prepared by rf-sputtering were investigated. The addition of Cu to Sm-Co film had the effect of decrement of crystallization temperature. The Sm28Co39Cu13 film annealed for 1 h at 623 K showed a reversible demagnetization curve with 82% springback ratio of [Mr' -M(H)]/[Mr-M(H)] and a high coercivity of 2480 kA·m-1. This film was found to be an exchange-spring magnet film composed of the hard magnetic phase such as SmCo5 and Sm2Co7 phases and a soft magnetic phase of Co. Sm28Co59Cu13/Co(x nm) multilayered film whose Co thickness was from 0 to 15 nm was also found to be an exchangespring magnet film.

本文言語英語
ページ(範囲)302-307
ページ数6
ジャーナルMaterials Transactions, JIM
39
2
DOI
出版ステータス出版済み - 2 1998
外部発表はい

All Science Journal Classification (ASJC) codes

  • Engineering(all)

フィンガープリント 「Magnetic properties of Sm-Co-Cu and Sm-Co-Cu/Co exchange-spring films with high coercivity」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル