Mechanical properties and microstructures of Al-Fe alloys processed by high-pressure torsion

Jorge M. Cubero-Sesin, Zenji Horita

研究成果: ジャーナルへの寄稿記事

29 引用 (Scopus)

抄録

Al-Fe alloys in the form of thin disks 10 mm in diameter, with Fe nominal weight fractions of 0.5, 1, 2, and 5 pct, were extracted from bulk-extruded rods and processed by high-pressure torsion (HPT). A group of these bulk samples was processed in an as-received state, whereas another group was annealed at 773 K (500 °C) for a period of 1 hour, prior to the application of HPT. An additional set of samples was prepared by mixing high-purity powders with similar Fe contents and consolidated directly in the HPT facility. The samples were processed up to 10 revolutions. Vickers microhardness, tensile strength, and elongation to failure were evaluated for all cases along with observations of the Al matrix by transmission electron microscopy (TEM). Basic characterization of the microstructures was carried out by X-ray diffraction (XRD) and optical microscopy (OM). Significant strengthening with ductility retained was achieved in the bulk samples as a consequence of grain refinement and dispersion of intermetallic phases. Powder samples had a more gradual increase in strength but increased ductility as a result of the imposed strain.

元の言語英語
ページ(範囲)5182-5192
ページ数11
ジャーナルMetallurgical and Materials Transactions A: Physical Metallurgy and Materials Science
43
発行部数13
DOI
出版物ステータス出版済み - 12 1 2012

Fingerprint

Torsional stress
torsion
mechanical properties
Mechanical properties
Powders
microstructure
Microstructure
Ductility
ductility
Grain refinement
Microhardness
Intermetallics
Optical microscopy
Elongation
Tensile strength
Transmission electron microscopy
X ray diffraction
microhardness
tensile strength
elongation

All Science Journal Classification (ASJC) codes

  • Condensed Matter Physics
  • Metals and Alloys
  • Mechanics of Materials

これを引用

Mechanical properties and microstructures of Al-Fe alloys processed by high-pressure torsion. / Cubero-Sesin, Jorge M.; Horita, Zenji.

:: Metallurgical and Materials Transactions A: Physical Metallurgy and Materials Science, 巻 43, 番号 13, 01.12.2012, p. 5182-5192.

研究成果: ジャーナルへの寄稿記事

@article{d233c9f88a4e4329ad01ad7fd5f7dc46,
title = "Mechanical properties and microstructures of Al-Fe alloys processed by high-pressure torsion",
abstract = "Al-Fe alloys in the form of thin disks 10 mm in diameter, with Fe nominal weight fractions of 0.5, 1, 2, and 5 pct, were extracted from bulk-extruded rods and processed by high-pressure torsion (HPT). A group of these bulk samples was processed in an as-received state, whereas another group was annealed at 773 K (500 °C) for a period of 1 hour, prior to the application of HPT. An additional set of samples was prepared by mixing high-purity powders with similar Fe contents and consolidated directly in the HPT facility. The samples were processed up to 10 revolutions. Vickers microhardness, tensile strength, and elongation to failure were evaluated for all cases along with observations of the Al matrix by transmission electron microscopy (TEM). Basic characterization of the microstructures was carried out by X-ray diffraction (XRD) and optical microscopy (OM). Significant strengthening with ductility retained was achieved in the bulk samples as a consequence of grain refinement and dispersion of intermetallic phases. Powder samples had a more gradual increase in strength but increased ductility as a result of the imposed strain.",
author = "Cubero-Sesin, {Jorge M.} and Zenji Horita",
year = "2012",
month = "12",
day = "1",
doi = "10.1007/s11661-012-1341-z",
language = "English",
volume = "43",
pages = "5182--5192",
journal = "Metallurgical and Materials Transactions A: Physical Metallurgy and Materials Science",
issn = "1073-5623",
publisher = "Springer Boston",
number = "13",

}

TY - JOUR

T1 - Mechanical properties and microstructures of Al-Fe alloys processed by high-pressure torsion

AU - Cubero-Sesin, Jorge M.

AU - Horita, Zenji

PY - 2012/12/1

Y1 - 2012/12/1

N2 - Al-Fe alloys in the form of thin disks 10 mm in diameter, with Fe nominal weight fractions of 0.5, 1, 2, and 5 pct, were extracted from bulk-extruded rods and processed by high-pressure torsion (HPT). A group of these bulk samples was processed in an as-received state, whereas another group was annealed at 773 K (500 °C) for a period of 1 hour, prior to the application of HPT. An additional set of samples was prepared by mixing high-purity powders with similar Fe contents and consolidated directly in the HPT facility. The samples were processed up to 10 revolutions. Vickers microhardness, tensile strength, and elongation to failure were evaluated for all cases along with observations of the Al matrix by transmission electron microscopy (TEM). Basic characterization of the microstructures was carried out by X-ray diffraction (XRD) and optical microscopy (OM). Significant strengthening with ductility retained was achieved in the bulk samples as a consequence of grain refinement and dispersion of intermetallic phases. Powder samples had a more gradual increase in strength but increased ductility as a result of the imposed strain.

AB - Al-Fe alloys in the form of thin disks 10 mm in diameter, with Fe nominal weight fractions of 0.5, 1, 2, and 5 pct, were extracted from bulk-extruded rods and processed by high-pressure torsion (HPT). A group of these bulk samples was processed in an as-received state, whereas another group was annealed at 773 K (500 °C) for a period of 1 hour, prior to the application of HPT. An additional set of samples was prepared by mixing high-purity powders with similar Fe contents and consolidated directly in the HPT facility. The samples were processed up to 10 revolutions. Vickers microhardness, tensile strength, and elongation to failure were evaluated for all cases along with observations of the Al matrix by transmission electron microscopy (TEM). Basic characterization of the microstructures was carried out by X-ray diffraction (XRD) and optical microscopy (OM). Significant strengthening with ductility retained was achieved in the bulk samples as a consequence of grain refinement and dispersion of intermetallic phases. Powder samples had a more gradual increase in strength but increased ductility as a result of the imposed strain.

UR - http://www.scopus.com/inward/record.url?scp=84870394997&partnerID=8YFLogxK

UR - http://www.scopus.com/inward/citedby.url?scp=84870394997&partnerID=8YFLogxK

U2 - 10.1007/s11661-012-1341-z

DO - 10.1007/s11661-012-1341-z

M3 - Article

AN - SCOPUS:84870394997

VL - 43

SP - 5182

EP - 5192

JO - Metallurgical and Materials Transactions A: Physical Metallurgy and Materials Science

JF - Metallurgical and Materials Transactions A: Physical Metallurgy and Materials Science

SN - 1073-5623

IS - 13

ER -