Micromechanics and numerical modelling of the hydrogen-particle-matrix interactions in nickel-base alloys

Y. Liang, P. Sofronis

研究成果: ジャーナルへの寄稿学術誌査読

37 被引用数 (Scopus)

抄録

The mechanics of hydrogen-induced decohesion and subsequent void formation at the interface of an elastic inclusion embedded in ductile matrix was studied. The aim of the study was to understand the micromechanics of hydrogen embrittlement in nickel-base alloys that fail by ductile intergranular fracture initiating at grain boundary carbides. It was found that hydrogen by weakening the interface promotes plastic flow localization in the surrounding matrix.

本文言語英語
ページ(範囲)523-551
ページ数29
ジャーナルModelling and Simulation in Materials Science and Engineering
11
4
DOI
出版ステータス出版済み - 7月 2003
外部発表はい

!!!All Science Journal Classification (ASJC) codes

  • モデリングとシミュレーション
  • 材料科学(全般)
  • 凝縮系物理学
  • 材料力学
  • コンピュータ サイエンスの応用

フィンガープリント

「Micromechanics and numerical modelling of the hydrogen-particle-matrix interactions in nickel-base alloys」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル