Microscopic Deformation Behavior Observation of Lamellar Pearlite during Plastic Deformation

Yu Sakoda, Suguru Kashiwagi, Shigeru Hamada, Hiroshi Noguchi

研究成果: Contribution to journalArticle査読

抄録

The fatigue ratio of lamellar pearlite steel used for railroad rails is lower than the ratio of general steels. The reason for this has not yet been clarified. It is reported that the direction of the lamellar microstructure in the lamellar pearlite steel affects the fatigue characteristics. In order to clarify the microscopic deformation behavior of the lamellar microstructure considered to affect the fatigue characteristics, static tensile tests of the lamellar pearlite steel were conducted. Using the plastic replica technique, the microscopic deformation behavior i.e. the initiation and propagation of microcracks was observed. Based on the experimental results, transgranular cracks and intergranular cracks were observed. The obtained main results are as follows.<br>(1) The transgranular crack originated in the discontinuous area in the lamellar pearlite microstructure. The transgranular crack initiates in a 45 degree direction to the axis of tension. The transgranular crack does not break through the grain boundary.<br>(2) The intergranular crack does not propagate, but opens.<br>(3) The difference in the material characteristics affected by heat treatment is the total strain of the crack initiation.
本文言語英語
ページ(範囲)137-144
ページ数8
ジャーナルJournal of Solid Mechanics and Materials Engineering
2
1
DOI
出版ステータス出版済み - 2008

フィンガープリント 「Microscopic Deformation Behavior Observation of Lamellar Pearlite during Plastic Deformation」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル