Microscopic observation of SOFC anodes under operation with hydrocarbon fuels

Tatsuya Kawada, Keiji Yashiro, Tomoaki Taura, Kenichiro Takeda, Atsushi Kaimai, Hiroshige Matsumoto, Junichiro Mizusaki, H. Yugami

研究成果: 著書/レポートタイプへの貢献会議での発言

4 引用 (Scopus)

抄録

Carbon deposition on a SOFC anode was investigated under direct hydrocarbon fueling condition. Microscopic behaviors were observed with a newly designed sample holder that enabled in-situ observation of an electrode in operation under controlled atmosphere at elevated temperatures. The preferential carbon deposition site, the structure of the deposited carbon, and the chemical or electrochemical re-oxidation processes were investigated with an optical microscope combined with a laser Raman microscope. Color and morphology change of the electrode surface was recorded with a CCD camera, and the deposited materials were identified with a laser Raman microscope. A nickel micro grid was used as a model electrode of a well-defined microstructure. When the cell was kept at an open circuit condition in methane, carbon started to deposit on the surface of Ni grid electrode. The deposition of carbon was clearly observed as the change in the reflection on the nickel surface by optical microscope as well as by the appearance of the specific peak at ∼1560 cm-1 in Raman spectroscopy. The deposited carbon was in the form of graphite on the nickel grid electrode. The carbon coverage on the surface was not uniform but varied from grain to grain. When a certain anodic overpotential (e.g. 200 mV) was applied to the electrode, the carbon disappeared gradually from the edge of the electrode i.e. from the electrode/electrolyte boundary where oxygen was supplied electrochemically. It is the first in-situ observation of the electrochemical carbon oxidation in a real operation condition.

元の言語英語
ホスト出版物のタイトルFuel Cell Science, Engineering and Technology - 2004
編集者R.K. Shah, S.G. Kandlikar
ページ53-59
ページ数7
出版物ステータス出版済み - 9 13 2004
外部発表Yes
イベントSecond International Conference on Fuel Cell Science, Engineering and Technology - Rochester, NY, 米国
継続期間: 6 14 20046 16 2004

出版物シリーズ

名前Fuel Cell Science, Engineering and Technology - 2004

その他

その他Second International Conference on Fuel Cell Science, Engineering and Technology
米国
Rochester, NY
期間6/14/046/16/04

Fingerprint

Solid oxide fuel cells (SOFC)
Anodes
Hydrocarbons
Carbon
Electrodes
Microscopes
Nickel
Oxidation
Fueling
Lasers
CCD cameras
Raman spectroscopy
Methane
Graphite
Deposits
Electrolytes
Protective atmospheres
Color
Microstructure
Oxygen

All Science Journal Classification (ASJC) codes

  • Engineering(all)

これを引用

Kawada, T., Yashiro, K., Taura, T., Takeda, K., Kaimai, A., Matsumoto, H., ... Yugami, H. (2004). Microscopic observation of SOFC anodes under operation with hydrocarbon fuels. : R. K. Shah, & S. G. Kandlikar (版), Fuel Cell Science, Engineering and Technology - 2004 (pp. 53-59). (Fuel Cell Science, Engineering and Technology - 2004).

Microscopic observation of SOFC anodes under operation with hydrocarbon fuels. / Kawada, Tatsuya; Yashiro, Keiji; Taura, Tomoaki; Takeda, Kenichiro; Kaimai, Atsushi; Matsumoto, Hiroshige; Mizusaki, Junichiro; Yugami, H.

Fuel Cell Science, Engineering and Technology - 2004. 版 / R.K. Shah; S.G. Kandlikar. 2004. p. 53-59 (Fuel Cell Science, Engineering and Technology - 2004).

研究成果: 著書/レポートタイプへの貢献会議での発言

Kawada, T, Yashiro, K, Taura, T, Takeda, K, Kaimai, A, Matsumoto, H, Mizusaki, J & Yugami, H 2004, Microscopic observation of SOFC anodes under operation with hydrocarbon fuels. : RK Shah & SG Kandlikar (版), Fuel Cell Science, Engineering and Technology - 2004. Fuel Cell Science, Engineering and Technology - 2004, pp. 53-59, Second International Conference on Fuel Cell Science, Engineering and Technology, Rochester, NY, 米国, 6/14/04.
Kawada T, Yashiro K, Taura T, Takeda K, Kaimai A, Matsumoto H その他. Microscopic observation of SOFC anodes under operation with hydrocarbon fuels. : Shah RK, Kandlikar SG, 編集者, Fuel Cell Science, Engineering and Technology - 2004. 2004. p. 53-59. (Fuel Cell Science, Engineering and Technology - 2004).
Kawada, Tatsuya ; Yashiro, Keiji ; Taura, Tomoaki ; Takeda, Kenichiro ; Kaimai, Atsushi ; Matsumoto, Hiroshige ; Mizusaki, Junichiro ; Yugami, H. / Microscopic observation of SOFC anodes under operation with hydrocarbon fuels. Fuel Cell Science, Engineering and Technology - 2004. 編集者 / R.K. Shah ; S.G. Kandlikar. 2004. pp. 53-59 (Fuel Cell Science, Engineering and Technology - 2004).
@inproceedings{8eb58d7c169b450c863a07c756f0115a,
title = "Microscopic observation of SOFC anodes under operation with hydrocarbon fuels",
abstract = "Carbon deposition on a SOFC anode was investigated under direct hydrocarbon fueling condition. Microscopic behaviors were observed with a newly designed sample holder that enabled in-situ observation of an electrode in operation under controlled atmosphere at elevated temperatures. The preferential carbon deposition site, the structure of the deposited carbon, and the chemical or electrochemical re-oxidation processes were investigated with an optical microscope combined with a laser Raman microscope. Color and morphology change of the electrode surface was recorded with a CCD camera, and the deposited materials were identified with a laser Raman microscope. A nickel micro grid was used as a model electrode of a well-defined microstructure. When the cell was kept at an open circuit condition in methane, carbon started to deposit on the surface of Ni grid electrode. The deposition of carbon was clearly observed as the change in the reflection on the nickel surface by optical microscope as well as by the appearance of the specific peak at ∼1560 cm-1 in Raman spectroscopy. The deposited carbon was in the form of graphite on the nickel grid electrode. The carbon coverage on the surface was not uniform but varied from grain to grain. When a certain anodic overpotential (e.g. 200 mV) was applied to the electrode, the carbon disappeared gradually from the edge of the electrode i.e. from the electrode/electrolyte boundary where oxygen was supplied electrochemically. It is the first in-situ observation of the electrochemical carbon oxidation in a real operation condition.",
author = "Tatsuya Kawada and Keiji Yashiro and Tomoaki Taura and Kenichiro Takeda and Atsushi Kaimai and Hiroshige Matsumoto and Junichiro Mizusaki and H. Yugami",
year = "2004",
month = "9",
day = "13",
language = "English",
isbn = "0791841650",
series = "Fuel Cell Science, Engineering and Technology - 2004",
pages = "53--59",
editor = "R.K. Shah and S.G. Kandlikar",
booktitle = "Fuel Cell Science, Engineering and Technology - 2004",

}

TY - GEN

T1 - Microscopic observation of SOFC anodes under operation with hydrocarbon fuels

AU - Kawada, Tatsuya

AU - Yashiro, Keiji

AU - Taura, Tomoaki

AU - Takeda, Kenichiro

AU - Kaimai, Atsushi

AU - Matsumoto, Hiroshige

AU - Mizusaki, Junichiro

AU - Yugami, H.

PY - 2004/9/13

Y1 - 2004/9/13

N2 - Carbon deposition on a SOFC anode was investigated under direct hydrocarbon fueling condition. Microscopic behaviors were observed with a newly designed sample holder that enabled in-situ observation of an electrode in operation under controlled atmosphere at elevated temperatures. The preferential carbon deposition site, the structure of the deposited carbon, and the chemical or electrochemical re-oxidation processes were investigated with an optical microscope combined with a laser Raman microscope. Color and morphology change of the electrode surface was recorded with a CCD camera, and the deposited materials were identified with a laser Raman microscope. A nickel micro grid was used as a model electrode of a well-defined microstructure. When the cell was kept at an open circuit condition in methane, carbon started to deposit on the surface of Ni grid electrode. The deposition of carbon was clearly observed as the change in the reflection on the nickel surface by optical microscope as well as by the appearance of the specific peak at ∼1560 cm-1 in Raman spectroscopy. The deposited carbon was in the form of graphite on the nickel grid electrode. The carbon coverage on the surface was not uniform but varied from grain to grain. When a certain anodic overpotential (e.g. 200 mV) was applied to the electrode, the carbon disappeared gradually from the edge of the electrode i.e. from the electrode/electrolyte boundary where oxygen was supplied electrochemically. It is the first in-situ observation of the electrochemical carbon oxidation in a real operation condition.

AB - Carbon deposition on a SOFC anode was investigated under direct hydrocarbon fueling condition. Microscopic behaviors were observed with a newly designed sample holder that enabled in-situ observation of an electrode in operation under controlled atmosphere at elevated temperatures. The preferential carbon deposition site, the structure of the deposited carbon, and the chemical or electrochemical re-oxidation processes were investigated with an optical microscope combined with a laser Raman microscope. Color and morphology change of the electrode surface was recorded with a CCD camera, and the deposited materials were identified with a laser Raman microscope. A nickel micro grid was used as a model electrode of a well-defined microstructure. When the cell was kept at an open circuit condition in methane, carbon started to deposit on the surface of Ni grid electrode. The deposition of carbon was clearly observed as the change in the reflection on the nickel surface by optical microscope as well as by the appearance of the specific peak at ∼1560 cm-1 in Raman spectroscopy. The deposited carbon was in the form of graphite on the nickel grid electrode. The carbon coverage on the surface was not uniform but varied from grain to grain. When a certain anodic overpotential (e.g. 200 mV) was applied to the electrode, the carbon disappeared gradually from the edge of the electrode i.e. from the electrode/electrolyte boundary where oxygen was supplied electrochemically. It is the first in-situ observation of the electrochemical carbon oxidation in a real operation condition.

UR - http://www.scopus.com/inward/record.url?scp=4344635478&partnerID=8YFLogxK

UR - http://www.scopus.com/inward/citedby.url?scp=4344635478&partnerID=8YFLogxK

M3 - Conference contribution

AN - SCOPUS:4344635478

SN - 0791841650

SN - 9780791841655

T3 - Fuel Cell Science, Engineering and Technology - 2004

SP - 53

EP - 59

BT - Fuel Cell Science, Engineering and Technology - 2004

A2 - Shah, R.K.

A2 - Kandlikar, S.G.

ER -