Microstructures and Mechanical Properties in a Sintered Ti-13mass%Cr Alloy

Kouji Sugaya, Yasuyuki Ikeda, Setsuo Takaki

    研究成果: ジャーナルへの寄稿学術誌査読

    1 被引用数 (Scopus)

    抄録

    A Ti-13mass%Cr alloy, which is the eutectoid composition in Ti-Cr binary alloy, was prepared by the technique of elemental powder mixing and sintering in the temperature range of β(bcc) field. The microstructure of the sintered compacts was investigated by means of optical microscopy, EPMA analysis and thermal contraction test. Mechanical properties of sintered compacts were also examined in terms of the precipitation of ω phase which takes place during continuous cooling from sintering temperature. The structure of a compact at sintering temperature is of β phase, but during slow cooling after sintering, α phase precipitates on grain boundaries of β phase below β transus, and then ω phase precipitates in the β matrix below around 600K. As a result, a sintered compact is consisted of (β+ α+ω) three phases at room temperature. Sintered compacts cooled slowly from the β field undergo brittle fracture. This brittle fracture is attributed not to the precipitation of α phase at grain boundary, but to the precipitation of ω phase. The degree of the ω embrittlement was reduced when the cooling rate in the temperature below 600K was increased over 1K/s(Air cooling), and could be fully suppressed when it was over 50K/s(Oil quenching).

    本文言語英語
    ページ(範囲)964-969
    ページ数6
    ジャーナルJournal of the Japan Society of Powder and Powder Metallurgy
    41
    8
    DOI
    出版ステータス出版済み - 1994

    !!!All Science Journal Classification (ASJC) codes

    • 機械工学
    • 産業および生産工学
    • 金属および合金
    • 材料化学

    フィンガープリント

    「Microstructures and Mechanical Properties in a Sintered Ti-13mass%Cr Alloy」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

    引用スタイル