TY - JOUR
T1 - Microstructures of long-period stacking ordered phase of Mg-Zn-Y alloy
AU - Gao, Hongye
AU - Ikeda, Ken Ichi
AU - Morikawa, Tatsuya
AU - Higashida, Kenji
AU - Nakashima, Hideharu
PY - 2013
Y1 - 2013
N2 - The microstructures of α-Mg, long-period stacking ordered (LPSO) phases, and kink bands in a Mg-Y-Zn alloy were observed by transmission electron microscopy (TEM). The results showed that extruded Mg97Zn 1Y2 alloy included different kinds of phases: 2H-Mg, 2H-Mg with many stacking faults, 14H and 18R. Kink bands tended to occur in areas where there were many intermetallic compounds. The element distribution of Zn/Y/Mg in the LPSO phase including kink boundaries was also analyzed by scanning TEM energy dispersive X-ray spectroscopy. The results showed that the concentrations of atomic Zn/Y decreased, while the concentration of atomic Mg increased at kink boundaries. This can be understood in terms of the dislocation structure of kink boundaries where extended a-dislocations lying on sequential stacking faults in the LPSO phase cause the annihilation of Zn/Y-rich stacking faults between two partial dislocations.
AB - The microstructures of α-Mg, long-period stacking ordered (LPSO) phases, and kink bands in a Mg-Y-Zn alloy were observed by transmission electron microscopy (TEM). The results showed that extruded Mg97Zn 1Y2 alloy included different kinds of phases: 2H-Mg, 2H-Mg with many stacking faults, 14H and 18R. Kink bands tended to occur in areas where there were many intermetallic compounds. The element distribution of Zn/Y/Mg in the LPSO phase including kink boundaries was also analyzed by scanning TEM energy dispersive X-ray spectroscopy. The results showed that the concentrations of atomic Zn/Y decreased, while the concentration of atomic Mg increased at kink boundaries. This can be understood in terms of the dislocation structure of kink boundaries where extended a-dislocations lying on sequential stacking faults in the LPSO phase cause the annihilation of Zn/Y-rich stacking faults between two partial dislocations.
UR - http://www.scopus.com/inward/record.url?scp=84877754112&partnerID=8YFLogxK
UR - http://www.scopus.com/inward/citedby.url?scp=84877754112&partnerID=8YFLogxK
U2 - 10.2320/matertrans.MI201219
DO - 10.2320/matertrans.MI201219
M3 - Article
AN - SCOPUS:84877754112
SN - 0916-1821
VL - 54
SP - 632
EP - 635
JO - Materials Transactions
JF - Materials Transactions
IS - 5
ER -