Microstructures of superconducting joint between GdBa2Cu3Oy-coated conductors via additionally deposited precursor films

Tomohiro Miyajima, Ryo Teranishi, Syotaro Yasuyama, Yukio Sato, Kenji Kaneko, Takuya Maeda, Minoru Ochi, Kazuya Hiramatsu, Miyuki Nakamura, Valery Petrykin, Sergey Lee, Tatsunori Okada, Satoshi Awaji

    研究成果: Contribution to journalArticle査読

    4 被引用数 (Scopus)

    抄録

    Superconducting joints have been demanded to lengthen REBa2Cu3O y -coated conductors for electrical power applications. In this study, we propose a new joint method for GdBa2Cu3O y -coated conductors via crystallizing precursor films additionally deposited on the conductors. Two GdBa2Cu3O y -coated conductors with precursor films were placed in a face-to-face manner in a furnace, then they were crystallized under mechanical pressure to joint them. A superconducting joint was achieved with a high critical temperature of 90.8 K. Microstructural observation by a transmission electron microscope revealed that there were only a few pores at the joint boundary without a secondary phase having c-axis-oriented GdBa2Cu3O y

    本文言語英語
    論文番号050913
    ジャーナルJapanese journal of applied physics
    58
    5
    DOI
    出版ステータス出版済み - 2019

    All Science Journal Classification (ASJC) codes

    • 工学(全般)
    • 物理学および天文学(全般)

    フィンガープリント

    「Microstructures of superconducting joint between GdBa<sub>2</sub>Cu<sub>3</sub>O<sub>y</sub>-coated conductors via additionally deposited precursor films」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

    引用スタイル