Microtubular SOFC using doped LaGaO3 electrolyte film prepared with dip coating method

Kohei Hosoi, Jong Eun Hong, Takaaki Sakai, Shintaro Ida, Tatsumi Ishihara

研究成果: ジャーナルへの寄稿学術誌査読

4 被引用数 (Scopus)

抄録

Preparation of Microtubular cell using doped lanthanum gallate (LSGM) electrolyte with a dip coating and co-sintering process was studied. In order to suppress Ni diffusion from Ni-based anode substrate to LSGM electrolyte layer, Ti added La-doped ceria (Ti-LDC) was inserted as buffer layer. The amount of Ni diffused in LSGM electrolyte was investigated by EDX analysis as a function of sintering temperatures. It was found that sintering at 1350°C is suitable from the sintering density and the Ni diffusion. The cell sintered at 1350°C exhibited the higher power density than that of the conventional LSGM micro-tubular cell, even though a small amount of Ni diffusion was still observed at the Ti-LDC buffer layer/LSGM electrolyte interface. The microtubular cell with around 50μm thickness showed the open circuit potential higher than 1.0V and the maximum power density of 0.69, 0.31 and 0.12W/cm2 at 700, 600 and 500°C, respectively, were achieved.

本文言語英語
ページ(範囲)182-186
ページ数5
ジャーナルJournal of the Ceramic Society of Japan
123
1436
DOI
出版ステータス出版済み - 4月 1 2015

!!!All Science Journal Classification (ASJC) codes

  • セラミックおよび複合材料
  • 化学 (全般)
  • 凝縮系物理学
  • 材料化学

フィンガープリント

「Microtubular SOFC using doped LaGaO3 electrolyte film prepared with dip coating method」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル