Mode II負荷における疲労き裂進展機構に関する検討

濱田 繁, 末益 太郎, 小山 元道, 上田 正治, 野口 博司

研究成果: ジャーナルへの寄稿学術誌

抄録

<p>Research on "Mode II fatigue crack propagation" is being conducted by many researchers. However, its understanding has not progressed as much as that of Mode I. We think that this cause is the name: "Mode II fatigue crack propagation." Originally, Modes I and II represented the loading modes for still cracks in fracture mechanics, and not the fatigue crack propagation mechanism. There are many cases where the knowledge of fatigue crack propagation under Mode I loading is applied to that under Mode II loading without consideration. The rolling contact fatigue is a typical example of fatigue crack propagation under cyclic Mode II loading. In the region where the fatigue crack propagates, a large plastic deformation is caused by the rolling contact load. Therefore, it is necessary for the test method to reproduce the effects of an actual machine to test materials that exhibit large plastic deformation. Therefore, in this study, we aim to classify the fatigue crack propagation phenomena, regardless of Mode I and II loadings, and examine the mechanisms. To that end, we developed a novel test method that enables pure cyclic Mode II loading. We used a micro-thin film disc as a specimen, making it possible to cut out and test a part subjected to a large plastic deformation from the actual machine. By successive observation of the fatigue crack propagation behavior, we propose a crack propagation mechanism, namely, damage accumulation type fatigue crack propagation under Mode II loading, which is different from the opening type fatigue crack propagation.</p>
寄稿の翻訳タイトルExamination of fatigue crack propagation mechanism under cyclic Mode II loading.
本文言語日本語
ページ(範囲)OS0831
ジャーナルM&M材料力学カンファレンス
2018
0
DOI
出版ステータス出版済み - 2018

フィンガープリント

「Mode II負荷における疲労き裂進展機構に関する検討」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル