Modification of the interface nanostructure and magnetic properties in Nd-Fe-B thin films

Kunihiro Koike, Takanao Kusano, Daisuke Ogawa, Keisuke Kobayashi, Hiroaki Kato, Mikihiko Oogane, Takamichi Miyazaki, Yasuo Ando, Masaru Itakura

研究成果: Contribution to journalArticle査読

8 被引用数 (Scopus)

抄録

The effects of Nd2Fe14B grain size and Nd coating on the coercivity in sputter-deposited Nd-Fe-B/Nd thin films have been investigated in order to gain an insight into the coercivity mechanism of Nd-Fe-B magnets. Highly textured Nd2Fe14B particles were grown successfully on the MgO(100) single-crystal substrate with the Mo underlayer. As the Nd-Fe-B layer thickness tNFB was decreased from 70 to 5 nm, the coercivity Hc increased gradually from 6.5 to 16 kOe. By depositing the Nd overlayer onto these films and post-annealing at 500 °C, the Hc value further increased from 17.5 kOe (tNFB = 70 nm) to 26.2 kOe (tNFB = 5 nm). The amount of Hc increase by the combination of the Nd coating and post-annealing was about 10 kOe irrespective of the tNFB value. These results therefore suggest an independence of size and interface effects on the coercivity of Nd-Fe-B magnets.

本文言語英語
論文番号33
ジャーナルNanoscale Research Letters
11
1
DOI
出版ステータス出版済み - 2016

All Science Journal Classification (ASJC) codes

  • Materials Science(all)
  • Condensed Matter Physics

フィンガープリント 「Modification of the interface nanostructure and magnetic properties in Nd-Fe-B thin films」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル