Morphology, microstructure, and surface area of La-added MgFe2O4 powder

Kenji Obata, Akane Doi, Maiko Nishibori, Kengo Shimanoe, Takuya Suzuki, Shigenori Matsushima

研究成果: Contribution to journalArticle査読

抄録

La-added and pure MgFe2O4 powders were prepared from a malic acid complex, and the effect of La-adding on the microstructure and specific surface area of MgFe2O4 powder were examined. There were no traces of impurity phases for pure MgFe2O4 powder in the X-ray diffraction measurement after calcination in the range of 600 to 800°C. When La atoms were added to MgFe2O4, the crystallite growth of MgFe2O4 was suppressed remarkably, resulting in a higher specific surface area in comparison with the pure material, and the lattice volume increased. X-ray photoelectron spectroscopy measurements showed that the binding energies of Mg 2s, Fe 2p, O 1s, and La 3d signals were in good agreement with the Mg2+, Fe3+, O21, and La3+ valence states, respectively. Scanning electron microscopy observations revealed that MgFe2O4 powder shows an aggregation of granular particles and that the individual particles are tightly interconnected with each other, whereas smaller particles compared with pure MgFe2O4 were observed for the La-added powder. It was found from the N2 adsorption measurement, moreover, that the amount of mesopore increases with La addition.

本文言語英語
ページ(範囲)402-407
ページ数6
ジャーナルJournal of the Ceramic Society of Japan
126
5
DOI
出版ステータス出版済み - 5 2018

All Science Journal Classification (ASJC) codes

  • Ceramics and Composites
  • Chemistry(all)
  • Condensed Matter Physics
  • Materials Chemistry

フィンガープリント 「Morphology, microstructure, and surface area of La-added MgFe<sub>2</sub>O<sub>4</sub> powder」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル