Multi-stage coking for increased tar yield and formed coke of high strength. 2. Rapid heating carbonization in the multi-stage coking of weathered coal blends

Isao Mochida, Naoki Motoshima, Yozo Korai, Hisashi Nakagawara

研究成果: Contribution to journalArticle査読

1 被引用数 (Scopus)

抄録

Two stage coking was applied to a blend of coking coals which had been stored in air for a long time. Although the blend provided a little less tetrahydrofuran-soluble (THFS) residue (13%) after the preheat treatment at 450 °C than the unoxidized coals, the formed coke of tetrahydrofuran-insoluble (THFI) residue failed to provide enough mechanical strength for blast furnace application after calcination at 1000 °C when the heating rate at the carbonization stage was 10 °C min-1. More rapid heating at 50 °C min-1 gave a high mechanical strength of 6 MPa by calcination at 700 °C, yielding 5% additional tar. The coke prepared from the extracted residue, through the controlled THF extraction yield of 10%, exhibited a high strength of 10 MPa after calcination at 800 °C when the carbonization heating rate was 10 °C min-1. Favourable influences of rapid heating against less fusible residue are discussed.

本文言語英語
ページ(範囲)784-786
ページ数3
ジャーナルFuel
69
6
DOI
出版ステータス出版済み - 6 1990

All Science Journal Classification (ASJC) codes

  • Chemical Engineering(all)
  • Fuel Technology
  • Energy Engineering and Power Technology
  • Organic Chemistry

フィンガープリント 「Multi-stage coking for increased tar yield and formed coke of high strength. 2. Rapid heating carbonization in the multi-stage coking of weathered coal blends」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル